论文部分内容阅读
对热轧后的Q960工程机械用钢进行了910℃保温20min的淬火和不同温度相同时间(40 min)的回火。研究了回火温度对组织和力学性能的影响。结果表明:钢淬火后的组织转变为板条马氏体,当回火温度为600℃时,钢的组织形成了回火索氏体;当回火温度为500℃时,试验钢具有优良的性能,即,R_(p0.2)=990 MPa,R_m=1086 MPa,A=17.8%,-40℃冲击功KV_2=68 J,满足GB/T16270-2009的要求。
The hot rolled Q960 construction machinery steels were tempered at 910 ℃ for 20 min and tempered at the same temperature (40 min) at different temperatures. The effect of tempering temperature on microstructure and mechanical properties was studied. The results show that the microstructure of the steel after quenching is transformed into lath martensite. When the tempering temperature is 600 ℃, the microstructure of the steel is tempered sorbite. When the tempering temperature is 500 ℃, the test steel has excellent Performance, that is, R_ (p0.2) = 990 MPa, R_m = 1086 MPa, A = 17.8%, and the impact energy at 40 ℃ KV_2 = 68 J, meet the requirements of GB / T16270-2009.