Vapor pressure of zirconium tetrachloride(ZrCl4) under vacuum and an argon pressure of 1×105Pa was measured.The thermochemical changes of ZrCl4 during evaporat
【机 构】
：
Institute of Nuclear and New Energy Technology
论文部分内容阅读
Vapor pressure of zirconium tetrachloride(ZrCl4) under vacuum and an argon pressure of 1×105Pa was measured.The thermochemical changes of ZrCl4 during evaporation were studied by thermogravimetry-differential thermal analysis(TG-DTA),X-ray diffractometry(XRD),scanning electron microscopy(SEM) and energy-dispersive X-ray(EDX) analysis.At the same temperature,vapor pressures of ZrCl4 under vacuum and an argon pressure of 1×105Pa are approximately the same.The vapor pressure exceeds 1×105Pa at 340℃.which is high enough for ZrC coating of coated fuel particles.ZrCl4 sample is hydrolyzed to some extent to give ZrO2 and HCl,which however,has little influence on vapor pressure of ZrCl4 at high temperature.No ZrCl3 and Cl2 are produced by decomposition of ZrCl4 during evaporation,which is confirmed by thermodynamic calculation.
其他文献
通过岩体结构调查、渗透张量计算和压水试验研究岩体渗透性能.结果发现,基岩裂隙潜水活跃带距地表70 m,是有毒元素向河流迁移的活跃通道,须采取河流改道、防渗等应急措施.地
在研究区域构造的基础上,通过实测地质剖面、采集定向标本、室内薄片观察、显微构造观测和岩组分析,研究地质构造对滑坡的控制作用。结果表明,宽大的北西向石狮村韧性剪切带
Isothermal and cyclic oxidizing behavior of Co-40Cr alloy and its lanthanum ion-implanted samples were studied at 1000℃ in the air by thermal-gravimetric analy
在分析西南喀斯特石山地区石漠化现状的基础上,认为这些地区所要建立的人地关系地域系统是耗散结构.根据耗散结构理论,建立和谐的人地关系地域系统,不仅需要不断地进行物质、
Based on the needs of green motor oil, and in order to improve the antioxidation properties of green lubricating oil, the effect of tocopherol antioxidation pro
In the squeeze casting process, loaded high pressure (over approximately 100 MPa) and high temperature influence the thermo-mechanical behavior and performance
The effects of bacterial strain,salinity and pH on the bioleaching of a complex ore using mesophilic and extremely thermophilic bacteria were investigated and t
Sintered Sm(CobalFexCu0.1Zr0.03)7.5 (x=0.09-0.21) permanent magnets with higher Fe content were found to have higher remanence Br and maximum energy product (BH
Sr2SiO4:xEu2+ phosphors were synthesized through the solid-state reaction technique. The crystal phase of Sr2SiO4:xEu2+ phosphor manipulated by Eu2+ concentrati
Dense membrane with the composition of SrFe0.6Cu0.3Ti0.1O3-δ (SFCTO) was prepared by solid state reaction method. Oxygen permeation flux through this membrane