Deterioration Mechanisms of Sulfate Attack on Concrete under Alternate Action
【机 构】
:
State Key Laboratory of Hydroscience and Engineering, Tsinghua University, Beijing 100084, China;Sch
【出 处】
:
武汉理工大学学报(材料科学版)(英文版)
【发表日期】
:
2010年2期
其他文献
Styrene-butadiene-styrene(SBS)modified bitumen crack filling material with or-ganophilic montmorillonite(OCFM)was prepared by melt blending.X-ray diffraction analysis shows that the interlayer spacing of organophilic montmorillonite(OMMT)in OCFM is widene
Cement paste with low water/cement ratio of 0.3 was observed using AFM.It is found that C-S-H has self similarity trait from scanning scale 20 μm×20 μm down to 300 nm×300 nm, and the feature of C-S-H at large scale is very similar to those smaller scales.
Melting Intercalation Method to Prepare Laurie Acid/Organophilic Montmorillonite Shape-stabilized Ph
The tensile and flexural properties of polyvinyl alcohol(PVA)fiber reinforced ultra high toughness cementitious composite(UHTCC)were investigated.The composite,tested at the age of 14 d,28 d and 56 d,shows extremely remarkable pseudo strain hardening beha