摘 要:混凝土拌合物的和易性又称为混凝土的工作性,是指混凝土在搅拌,运输,浇筑,振捣等过程中易于操作,并能获得质量均匀,成型密实的混凝土的性能。和易性是混凝土拌合物在施工操作时所表现的综合性能,它包括流动性,黏聚性和保水性三个方面。
关键词:混凝土拌合物和易性;主要因素;测定方法
The main factors affect the workability of concrete mixture and its measurement method
Yi ming ka re·ai sang, Xi ri ai li·yi ming
(Department of Water Resources in Xinjiang Kashgar River Basin Management Office, Xinjiang kashgar 844000)
Abstract:The workability of the concrete mixture, also known as concrete work, concrete during mixing, transportation, pouring, vibration, easy to operate, and can obtain uniform quality, forming a dense concrete performance. The workability of concrete mixture in the construction and operation of overall performance, which includes three aspects of mobility, cohesiveness and water retention.
Keywords:concrete mix workability; major factor; measurement method
1.影响混凝土拌合物和易性的主要因素
影响混凝土拌合物和易性的主要因素很多,其中主要有水泥浆用量,水灰比,砂率,水泥品种与性质,集料的种类与特征,外加剂,施工时的温度和时间等。
1.1水泥浆的稠度。水泥浆的稠度是由水灰比所决定。在水泥用量不变的情况下,水灰比愈小,水泥浆就愈稠,混凝土拌合物的流动性便愈小。当水灰比过小时,水泥浆干稠,混凝土拌合物的流动性过低,会使施工困难,不能保证混凝土的密实性。增加水灰比会使流动性加大,如果水灰比过大,又会造成混凝土拌合物的黏聚性不良,而产生流浆离析现象,并严重影响混凝土的强度。无论是水泥浆的多少,还是水泥浆的稀稠,实际上对混凝土拌合物的流动性起决定作用的是用水量的多少,用水量小则流动性小,混凝土不易密实;用水量大则流动性大,随着用水量再增大,混凝土拌合物的黏聚性和保水性常常随之恶化。因此,不应单纯增加用水量来调整混凝土拌合物的流动性,而应当在保持水灰比不变的条件下,用调整水泥浆量的办法来调整混凝土拌合物的流动性。
1.2水泥浆的流动性。混凝土拌合物中的水泥浆,赋予混凝土拌合物以一定的流动性。在水灰比不变的情况下,单位体积拌合物内,如果水泥浆愈多,则拌合物的流动性愈大。但若水泥浆过多,将会出现流浆现象,使拌合物的黏聚性变差,同时对混凝土的强度和内疚性也会产生一定的影响,且水泥用量也大;水泥浆过少,则不能填满集料空隙或不能很好地包裹集料表面,此时就会产生崩坍现象,凝聚性变差。因此,混凝土拌合物中水泥浆的含量应以满足流动性和强度的要求为宜,不宜过量。
1.3砂率。砂率是指混凝土中所用砂子质量占所用砂,石总质量的百分数,砂率对混凝土流动性及其他特征也有明显的影响。砂率太小,砂量不足,水泥浆不能填满石子颗粒间空隙,因而会降低拌合料的流动性,并产生分层,离析现象。砂率较大时,水泥砂浆在填满石子间空隙后还有多余,多余的砂浆会在石子颗粒间形成润滑层,使拌合料流动性大。但如果砂率过大时,水泥浆不足以包裹砂粒表面和填满砂粒之间的空隙,也会导致拌合料流动性减小。因此,砂率的大小应通过试验确定其最佳值。
1.4集料的种类与特征。在混凝土配合比相同的情况下,使用表面粗糙且多菱角的砂,石时拌合物的和易性较差。因此,采用多菱角的碎石时,应增大砂率和相应的水泥浆用量。采用级配不好的砂,石,其空隙率大。在同样的配合比的情况下,混凝土拌合物易产生离析,黏聚性及保水性能均为较差。因此尽量采用表面光滑,颗粒近似圆形,级配良好的集料拌制混凝土。
1.5时间与温度。搅拌完的混凝土拌合物,随着时间的延长而逐渐变得干稠,和易性较差,其原因部分水分洪水泥水化,部分水分被集料吸收,另一部分水分蒸发掉。由于水分减少,混凝土拌合物的流动度变小。随着温度的升高,混凝土拌合物的流动性要降低,温度每升高10℃,坍落度约减少为20mm。因此,在施工中为保证混凝土拌合物的和易性,要考虑时间和温度的影响,并采取相应的措施。
1.6外加剂。在拌制混凝土时,掺入适量的外加剂,能有效地改善混凝土施工的工艺性能。
如掺入加气剂,可以产生大量气泡,改善拌合料的和易性。如掺入减水剂,能使混凝土拌合料在不增加用水量的条件下降低水灰比,改善和易性,增加流动性。
2.混凝土拌合物和易性的测定方法
和易性是一项综合性指标,通常采用测定混凝土拌合物的流动性的同时,以至关经验评定凝聚性和保水性,来评价混凝土拌合物的和易性。混凝土流动性不同,其工作性的评定方法也不同,流动性大的可采用坍落度法;流动性小的可用维勃法稠度发。
2.1坍落度法。混凝土拌合物坍落度用坍落度筒来测定,将混凝土拌合料分三次装入坍落度筒中,每次装料约1/3筒高,捣棒岛插25下刮平后,将筒垂直提起,测定拌合物由于自重产生坍落的毫米数,称为坍落度,坍落度越大,表示混凝土拌合物的流动性越大。
在测定坍落度时,还需同时观察混凝土拌合物的黏聚性和保水性:提起坍落度筒后,轻拍混凝土侧面,不是均匀下沉,而是突然倒塌或者是部分崩溃,石子掉落,则为混凝土拌合物的黏聚性不良。如果有水析出说明保水性较差。
坍落度筒测定流动性的方法,只适用于粗集料粒径小于40mm,坍落度值不小于10mm的混凝土拌合物。
根据混凝土拌合物坍落度的大小将混凝土分为干硬性混凝土(坍落度小于10mm),粗性混凝土(坍落度10~90mm),流动性混凝土(坍落度100~150mm),大流动性混凝土(坍落度≥160mm)。
2.2维勃稠度法。干硬性混凝土的和易性用维勃稠度法
评定。测定时,在坍落度筒中按规定方法装满混凝土拌合物,提起坍落度筒,在混凝土拌合物试体顶面放一透明圆盘。开启振动台,同时秒表计时,到透明圆盘的底面完全为水泥浆所布满时,停止秒表,关闭振动台。此时认为混凝土拌合物已密实,所读秒数称为维勃稠度。
混凝土拌合物的按其维勃稠度值的大小。可分为4级,并应符合表的规定。
关键词:混凝土拌合物和易性;主要因素;测定方法
The main factors affect the workability of concrete mixture and its measurement method
Yi ming ka re·ai sang, Xi ri ai li·yi ming
(Department of Water Resources in Xinjiang Kashgar River Basin Management Office, Xinjiang kashgar 844000)
Abstract:The workability of the concrete mixture, also known as concrete work, concrete during mixing, transportation, pouring, vibration, easy to operate, and can obtain uniform quality, forming a dense concrete performance. The workability of concrete mixture in the construction and operation of overall performance, which includes three aspects of mobility, cohesiveness and water retention.
Keywords:concrete mix workability; major factor; measurement method
1.影响混凝土拌合物和易性的主要因素
影响混凝土拌合物和易性的主要因素很多,其中主要有水泥浆用量,水灰比,砂率,水泥品种与性质,集料的种类与特征,外加剂,施工时的温度和时间等。
1.1水泥浆的稠度。水泥浆的稠度是由水灰比所决定。在水泥用量不变的情况下,水灰比愈小,水泥浆就愈稠,混凝土拌合物的流动性便愈小。当水灰比过小时,水泥浆干稠,混凝土拌合物的流动性过低,会使施工困难,不能保证混凝土的密实性。增加水灰比会使流动性加大,如果水灰比过大,又会造成混凝土拌合物的黏聚性不良,而产生流浆离析现象,并严重影响混凝土的强度。无论是水泥浆的多少,还是水泥浆的稀稠,实际上对混凝土拌合物的流动性起决定作用的是用水量的多少,用水量小则流动性小,混凝土不易密实;用水量大则流动性大,随着用水量再增大,混凝土拌合物的黏聚性和保水性常常随之恶化。因此,不应单纯增加用水量来调整混凝土拌合物的流动性,而应当在保持水灰比不变的条件下,用调整水泥浆量的办法来调整混凝土拌合物的流动性。
1.2水泥浆的流动性。混凝土拌合物中的水泥浆,赋予混凝土拌合物以一定的流动性。在水灰比不变的情况下,单位体积拌合物内,如果水泥浆愈多,则拌合物的流动性愈大。但若水泥浆过多,将会出现流浆现象,使拌合物的黏聚性变差,同时对混凝土的强度和内疚性也会产生一定的影响,且水泥用量也大;水泥浆过少,则不能填满集料空隙或不能很好地包裹集料表面,此时就会产生崩坍现象,凝聚性变差。因此,混凝土拌合物中水泥浆的含量应以满足流动性和强度的要求为宜,不宜过量。
1.3砂率。砂率是指混凝土中所用砂子质量占所用砂,石总质量的百分数,砂率对混凝土流动性及其他特征也有明显的影响。砂率太小,砂量不足,水泥浆不能填满石子颗粒间空隙,因而会降低拌合料的流动性,并产生分层,离析现象。砂率较大时,水泥砂浆在填满石子间空隙后还有多余,多余的砂浆会在石子颗粒间形成润滑层,使拌合料流动性大。但如果砂率过大时,水泥浆不足以包裹砂粒表面和填满砂粒之间的空隙,也会导致拌合料流动性减小。因此,砂率的大小应通过试验确定其最佳值。
1.4集料的种类与特征。在混凝土配合比相同的情况下,使用表面粗糙且多菱角的砂,石时拌合物的和易性较差。因此,采用多菱角的碎石时,应增大砂率和相应的水泥浆用量。采用级配不好的砂,石,其空隙率大。在同样的配合比的情况下,混凝土拌合物易产生离析,黏聚性及保水性能均为较差。因此尽量采用表面光滑,颗粒近似圆形,级配良好的集料拌制混凝土。
1.5时间与温度。搅拌完的混凝土拌合物,随着时间的延长而逐渐变得干稠,和易性较差,其原因部分水分洪水泥水化,部分水分被集料吸收,另一部分水分蒸发掉。由于水分减少,混凝土拌合物的流动度变小。随着温度的升高,混凝土拌合物的流动性要降低,温度每升高10℃,坍落度约减少为20mm。因此,在施工中为保证混凝土拌合物的和易性,要考虑时间和温度的影响,并采取相应的措施。
1.6外加剂。在拌制混凝土时,掺入适量的外加剂,能有效地改善混凝土施工的工艺性能。
如掺入加气剂,可以产生大量气泡,改善拌合料的和易性。如掺入减水剂,能使混凝土拌合料在不增加用水量的条件下降低水灰比,改善和易性,增加流动性。
2.混凝土拌合物和易性的测定方法
和易性是一项综合性指标,通常采用测定混凝土拌合物的流动性的同时,以至关经验评定凝聚性和保水性,来评价混凝土拌合物的和易性。混凝土流动性不同,其工作性的评定方法也不同,流动性大的可采用坍落度法;流动性小的可用维勃法稠度发。
2.1坍落度法。混凝土拌合物坍落度用坍落度筒来测定,将混凝土拌合料分三次装入坍落度筒中,每次装料约1/3筒高,捣棒岛插25下刮平后,将筒垂直提起,测定拌合物由于自重产生坍落的毫米数,称为坍落度,坍落度越大,表示混凝土拌合物的流动性越大。
在测定坍落度时,还需同时观察混凝土拌合物的黏聚性和保水性:提起坍落度筒后,轻拍混凝土侧面,不是均匀下沉,而是突然倒塌或者是部分崩溃,石子掉落,则为混凝土拌合物的黏聚性不良。如果有水析出说明保水性较差。
坍落度筒测定流动性的方法,只适用于粗集料粒径小于40mm,坍落度值不小于10mm的混凝土拌合物。
根据混凝土拌合物坍落度的大小将混凝土分为干硬性混凝土(坍落度小于10mm),粗性混凝土(坍落度10~90mm),流动性混凝土(坍落度100~150mm),大流动性混凝土(坍落度≥160mm)。
2.2维勃稠度法。干硬性混凝土的和易性用维勃稠度法
评定。测定时,在坍落度筒中按规定方法装满混凝土拌合物,提起坍落度筒,在混凝土拌合物试体顶面放一透明圆盘。开启振动台,同时秒表计时,到透明圆盘的底面完全为水泥浆所布满时,停止秒表,关闭振动台。此时认为混凝土拌合物已密实,所读秒数称为维勃稠度。
混凝土拌合物的按其维勃稠度值的大小。可分为4级,并应符合表的规定。