A quaternary alloy (Al-5.0Cu-0.35Mn-0.25Ti, wt.%), having a similar chemical component with ZL205A, was prepared using a controlled diffusion solidification (CD
The grain refi nement limits of commercial pure Al inoculated by Al-5Ti-1B, Al-5Ti-0.25C and Al-5Ti-0.3C-0.2B master alloys were studied, and the infl uence of
The purpose of this study is to prepare a high-quality Al-11Si-1.5Cu-0.3Mg casting al oy with a good combination of strength and ductility. The microstructures
In the present research, the orthogonal experiment was carried out to investigate the influence of different austempering process parameters (i.e. austenitizing
The mechanism of stray grain formation at the platform of turbine blade simulator and the effect of withdrawal rate (V) on the stray grain phenomenon have been
A travelling magnetic field, a power ultrasonic field, and a compound field were used separately during the horizontal continuous casting process of Al-1wt.%Si
Soldering is a unique casting defect associated with die casting or metal mold casting of aluminum alloys. It occurs when molten aluminum sticks or solders the
The microstructures and crystal growth directions of permanent mould casting and directionally solidified Al-Mg alloys with different Mg contents have been inve
The preparation and solidification of metallic droplets attract more and more attention for their signifi cance in both engineering and scientifi c fi elds. In