【摘 要】
：
研究了重熔温度对粉末触变成形制备Ti@Al_3Ti_p/2024Al基复合材料组织与力学性能的影响。结果发现,随着重熔温度升高,初生相颗粒逐渐长大,Al_3Ti反应层逐渐增厚,材料从最初的
【机 构】
：
兰州理工大学有色金属先进材料加工与再利用国家重点实验室,兰州理工大学有色金属合金及加工教育部重点实验室,
论文部分内容阅读
研究了重熔温度对粉末触变成形制备Ti@Al_3Ti_p/2024Al基复合材料组织与力学性能的影响。结果发现,随着重熔温度升高,初生相颗粒逐渐长大,Al_3Ti反应层逐渐增厚,材料从最初的缺陷断裂转变为韧性断裂再转变为最后的脆性断裂。当重熔温度为645℃时,合金抗拉强度和伸长率都达到最高,分别为361 MPa和13.7%。
The effect of remelting temperature on microstructure and mechanical properties of Ti @ Al_3Ti_p / 2024Al matrix composites prepared by thixoforming was investigated. The results show that as the remelting temperature increases, the primary phase grains grow up and the Al 3 Ti reactive layer gradually thickens. The material changes from initial defect to ductile fracture and finally to brittle fracture. When the remelting temperature was 645 ℃, the tensile strength and elongation of the alloy reached the highest, which were 361 MPa and 13.7% respectively.
其他文献
对AZ31镁合金挤压型材实施了搅拌摩擦加工(Friction Stir Processing·FSP),利用光学显微镜和拉伸试验机研究了搅拌摩擦加工对试样加工硬化率及力学性能的影响。结果表明,AZ3
采用石墨型铸造工艺制备了大型薄壁钛合金头罩铸件。针对头罩高度大、壁薄的特点,设计了3套浇注系统:卧式阶梯式浇注系统、头锥置上顶注式浇注系统以及尾部朝上雨淋式浇注系
对填充片状铝粉的硅橡胶热接口材料进行了研究.分析了导热系数、击穿电压、拉伸强度等主要指标与复合片状铝粉的加入量之间的关系,并对其变化趋势进行了探讨.给出了该类型热
通过选择不同的挤压温度、挤压比和挤压速度,研究了挤压温度、挤压比和挤压速度对Gr.38钛合金管材组织和性能的影响。结果表明,当挤压温度、挤压比或挤压速度提高时,α相的含
从流变学和耐蚀性两方面对半固态Mg-Al-Zn合金进行了设计和分析。结果显示,当Al含量在6%~11%之间,固相率为30%~60%时,随着Al含量增加,固相率随温度变化的敏感性降低,凝固温度
研究了IMI834钛合金棒材经不同固溶和时效热处理后的显微组织和性能,以期获得固溶和时效与合金组织性能的对应关系以及最优热处理工艺。结果表明,抗拉强度和屈服强度随固溶温
采用三维打印技术(3DP)和液滴按需喷射技术(DOD),以铸造蜡为对象,采用仿真与试验相结合的方法,以喷嘴温度、成形速度、供料压力为研究因素,研究蜡模的打印精度。首先通过正交
采用Gleeble-3500热模拟试验机对6061铝合金进行等温热压缩试验,研究变形温度为300~450℃、应变速率为0.01~10s-1、压缩量为60%条件下合金的热变形特性,分析其高温流变应力行
提出了坩埚半径的设计思路,研究了坩埚半径对电磁搅拌制备半固态A356铝合金浆料时磁感应强度和电磁力分布的影响。通过ANSYS 15.0模拟了不同坩埚半径中半固态A356铝合金浆料
请下载后查看，本文暂不支持在线获取查看简介。
Please download to view, this article does not support online access to view profile.