【摘 要】
：
通过接枝共聚法制备了PEG/CDA复合高分子固-固相变材料,用DSC差示扫描量热法及FTIR对其进行了表征,用正交试验法L9(34)研究了PEG分子量、PEG/CDA的质量比对相变材料储热性能,
【机 构】
：
陕西理工学院材料科学与工程学院,陕西理工学院材料科学与工程学院,陕西理工学院材料科学与工程学院,陕西理工学院材料科学与工程学院 汉中723003,汉中723003,汉中723003,汉中723003
论文部分内容阅读
通过接枝共聚法制备了PEG/CDA复合高分子固-固相变材料,用DSC差示扫描量热法及FTIR对其进行了表征,用正交试验法L9(34)研究了PEG分子量、PEG/CDA的质量比对相变材料储热性能,相变温度等的影响,以及反应时间对接枝反应的影响。结果表明,当PEG相对分子量为6000,PEG/CDA质量比为9∶1,接枝反应时间为150min时,材料的储热性最好。
The PEG / CDA composite solid-solid phase-change materials were prepared by graft copolymerization. Their structures were characterized by DSC differential scanning calorimetry and FTIR. The effects of PEG molecular weight, The effect of mass ratio of PEG / CDA on the heat storage performance, phase transition temperature and other properties of phase change materials, and the effect of reaction time on graft reaction. The results showed that when the relative molecular weight of PEG was 6000, the mass ratio of PEG / CDA was 9:1, the graft reaction time was 150min, the heat storage property of the material was the best.
其他文献
技术哲学不仅为新的科学技术关系提供了依据，而且为解读科技史带来了全新的视角。本文通过对美国科技发展历程的历时态解读，揭示了科学与技术关系的演变，并将其发展阶段中的科学
肯尼亚基苏木公路项目位于肯尼亚西部地区尼亚萨省基苏木市，是肯尼亚北方走廊公路网一部分。项目全长24公里，共有桥梁9座，其中过河桥2座。桥梁上部结构形式为预应力空心板梁，桥面
鉴于传统插引方法的低效以及现在市面上的插引机在工作过程中，不能对插饼进行计数而采用手工计数、噪声大、产生高温后不能实时报警以及系统卡引不能及时监控停机等问题而发明
文章结合光栅光阀响应时间短和反射光栅衍射效率高的特点,设计了一种光栅光阀式1×3微型光开关。理论计算和对比实验表明,在波长为1.3μm,闪耀角和入射角分别为5.4°和0°的
目的：探讨临床护士如何才能避免护患之间的纠纷。方法：通过对各种护患纠纷发生的原因进行分析，找出预防方法，结果：找出临床护理工作中护患纠纷发生的原因，提高护理质量，让患者满意。
目的：探讨医护合作分级护理模式在急诊留观患者护理中的应用及效果。方法：选取2013年1月至5月东院收治的88名急诊留观患者为实验组，实施医护合作分级护理模式，选取同期西院未实施
目的 探讨恩必普联合小剂量阿司匹林治疗脑梗死的治疗效果.方法 选取100例脑梗死患者.随机分为治疗组和对照组各50例,均给疏血通注射液静滴,每日1次；在此基础上治疗组给予恩必
目的 观察丹参川穹嗪治疗糖尿病周围神经病变的疗效及安全性,评价其临床应用价值.方法 将78例糖尿病周围神经病变病人随机分两组,对照组给予糖尿病教育,饮食控制,适量运动,胰
目的 观察阿立哌唑联合氯氮平治疗女性精神分裂症的疗效和安全性.方法 利用随机对照的方法,按照CCMD-3诊断标准选择女性精神分裂症住院患者40例,随机分为2组,两组均口服阿立
在一冷态循环流化床实验装置上,考察了一定颗粒原始存料量下,流化风速和回料风量对物料在循环系统中的分布和循环流率的影响.实验结果表明,当固定回料风量时,系统颗粒循环量