采用干法高能球磨-一步固相反应合成LiFe1-xMgxPO4(x=0,0.01,0.05,0.10和0.20)正极材料。利用x射线衍射仪、扫描电镜和能量色散谱表征样品的晶体结构、形貌和Mg元素分布,并研究Mg掺杂量对LiFePO4材料电化学性能的影响。结果表明,制备的LiFe1-xMgxPO4(0≤x≤0.10)为纯相,且LiFe1-xMgxPO4(x=0,0.01,0.05,0.10和0.20)晶粒尺寸随掺杂量的增大而增大。LiFe1-xMgxPO4的放电容量最佳,室温0.1c倍率下充放电其首次放电容量