Polystyrene(PSt)microspheres with diameter of 375 nm to be used as the seeds for seeded emulsion polymerization were prepared via emulsion polymerization using potassium persulfate(KPS)as initiator in ethanol-water mixed solvents.Emulsifier-free seeded emulsion copolymerization of styrene(St)with acrylonitrile(AN)was carried out in the presence of poly(ethylene glycol)monomethoxymonomethacrylate(PEGm) macromonomer as reactive stabilizer and 2,2-azobisisobutyronitrile(AIBN)as initiator to obtain submicron-sized PEGm graft poly(styrene-co- acrylonitrile)(PEGm-g-PSAN)composite particles with unique morphology.Scanning electron microscopy(SEM)indicated that St and AN together contributed to forming the unusual morphology.The concentration of St and AN,total monomer concentration,initiator type and the monomer adding method remarkably affected the morphology of the composite polymer particles.
Polystyrene (PSt) microspheres with diameter of 375 nm to be used as the seeds for seeded emulsion polymerization were prepared via emulsion polymerization using potassium persulfate (KPS) as initiator in ethanol-water mixed solvents. Emulsifier-free seeded emulsion copolymerization of styrene (St ) with acrylonitrile (AN) was carried out in the presence of poly (ethylene glycol) monomethoxymonomethacrylate (PEGm) macromonomer as reactive stabilizer and 2,2-azobisisobutyronitrile (AIBN) as initiator to obtain submicron-sized PEGm graft poly acrylonitrile) (PEGm-g-PSAN) composite particles with unique morphology. Scanning electron microscopy (SEM) indicated that St and AN together contributed to forming the unusual morphology. The concentration of St and AN, total monomer concentration, initiator type and the monomer adding method remarkably affected the morphology of the composite polymer particles.