【摘 要】
:
本工作主要是通过微量化学分析、X射线、金属薄膜透射电镜、电子衍射分析和X射线衍射能谱分析的方法,对38Fe-40Ni-14Cr为基的高温合金,在750℃长期时效后组织变化及其对室温
【出 处】
:
冶金分析与测试(冶金物理测试分册)
论文部分内容阅读
本工作主要是通过微量化学分析、X射线、金属薄膜透射电镜、电子衍射分析和X射线衍射能谱分析的方法,对38Fe-40Ni-14Cr为基的高温合金,在750℃长期时效后组织变化及其对室温冲击韧性的影响进行了研究。一、试验过程合金经真空感应熔炼+电渣重熔,锭重400kg。锻成80mm方坯,再热轧成机φ9mm的圆棒。合金的化学成分列于表1。合金标准热处理工艺为1150℃2h空冷,800℃ 16h空冷。试样经标准处理后再经长期时效处理:(1)
In this work, microstructures of 38Fe-40Ni-14Cr-based superalloy were investigated by means of micro-chemical analysis, X-ray, TEM, EDS and XRD. And its impact on toughness at room temperature were studied. First, the test process alloy vacuum induction melting + ESR, spindle weight 400kg. Forged into 80mm billet, and then hot-rolled machine φ9mm round bar. The chemical composition of the alloy is shown in Table 1. Alloy standard heat treatment process is 1150 ℃ 2h air cooling, 800 ℃ 16h air cooling. After the sample is treated by standard aging treatment: (1)
其他文献
随着基因组学的发展,制药工业以及农、化、食品工业将进行大规模重组、重叠,而形成了边界模糊交插渗透的新兴领域——生命科学工业(Life Science Industry)。从此,人们将可
为了探讨提钒脱硅同时进行的可能性,本文采用FeO—SiO_2熔剂处理含钒铁水,对钒,硅、碳、磷的氧化行为进行了研究。并对铁水中的初始硅含量,终渣中的氧化铁和二氧化硅之比对提
首次提出关于多层漆膜中的水汽渗透常数的计算式,并通过实验进行了其准确性的验证,结果表明是可行的。
For the first time, the calculation formula of the water vapor p
用硬质材料螺纹状修整工具在砂轮外圆上边旋转边挤压,修出螺纹形状。再用整形过的砂轮磨削较软的油石,达到修锐的目的。这种方法的好处是,经济,砂轮耐用,表面上的金刚石或CBN
磨粒磨损过程是通过显微切削,微小碎粒从材料上断裂的过程。该过程可以分为切断和正断两种,一般情况下磨粒磨损是以切断为主.正断为辅,此时耐磨性取决于材料的切断强度t_k,
本文研究了SNIF-TX型净化装置在用氮气处理铝合金熔体时,产生的黑褐色夹杂物的组织特征和本质,找到了分离这种夹杂物的方法和防止它进入铸锭的措施,对国内SNIF净化设备的使用
本文就等温淬火对二种相似化学成份的灰铁的显微组织和机械性能的作用进行了评价。用于金相、X射线、硬度和抗拉强度试验的试样在843℃奥氏体化,并在288~371℃温度范围内等温
黄铜是由铜和锌两种金属所组成的合金,具有耐蚀、强度高和工艺性能好等优点,然而在使用过程中易于脱锌,降低了其耐蚀性能。而在其中加入少量的合金元素锡及砷,就能极大地抑
在机械行业中,推广应用微电脑新技术,实现机电一体化,特别对原设备进行简易的数控技术改造,是适应我国当前工业生产需要的一条行之有效的途径。今年,我厂在南京微分电机厂和
通常采用GCrl5钢锻造的轴承套圈都要进行球化退火,以获得均匀分布球化组织。球化退火工艺是较为复杂的,影响球化退火质量的因素很多,特别是采用箱式电阻炉进行退火处理,更应