采用快速凝固技术在AL-3.18Ti-0.65C合金(Wt%)合金中获得了是弥散分布的TiC相颗粒.结合常规和快速凝固组织的分析对比,研究和探讨了相的形成过程和机制;快凝技术为研制AL/TiC自生复合材料开辟了新的途径.
The rapid solidification technique was used to obtain TiC particles dispersed in Al-3.18Ti-0.65C alloy (Wt%). Based on the analysis and comparison of conventional and rapid solidified tissues, the formation process and mechanism of the phases were studied and discussed. The fast-freezing technique opened up a new way for the development of AL / TiC composites.