In order to develop the ignition-proof magnesium alloy, the effect of alloying elements, Ca and Y, on the oxidation behavior of AZ91 magnesium alloy at elevated
【机 构】
：
State Key Laboratory of Solidification Processing
论文部分内容阅读
In order to develop the ignition-proof magnesium alloy, the effect of alloying elements, Ca and Y, on the oxidation behavior of AZ91 magnesium alloy at elevated temperatures was investigated. The ignition-proof performance, oxide products and oxidation kinetics of Ca- and Y-containing AZ91 alloys were studied. The results indicate that the proper addition of Ca can increase the ignition point of AZ91 alloy greatly. However, the oxide film of Ca-bearing AZ91 alloy formed at elevated temperature is thick and brittle, which is prone to crack in melting and cooling process. In addition, the oxide film of AZ91-xCa alloy is incompact and cannot inhibit the diffusion of reaction particles. The oxide film of AZ91-xCa alloy turns to thin and plastic one after Y is added, and the density of the oxide film increases greatly due to the formation of composite oxide film composed of MgO, CaO and Y2O3.
其他文献
Micrometer and nanometer Cr particles were co-deposited with Ni by electroplating from a nickel sulfate bath containing a certain content of Cr particles. Cr mi
La0.7-xSmx+0.02Ca0.3CrO3-δ(0≤x≤0.4) powders with A-site excessive perovskite structure were synthesized by auto-ignition process and characterized. X-ray dif
This investigation deals with the observations pertaining to the effects of specimen and slurry compositions as well as traversal distance on the slurry wear re
Commercial cathode material (LiCoO2) was modified by coating with a thin layer of SrO/Li2O/La2O3/Ta2O5/TiO2 for improving its performance in lithium ion battery
The present study is concerned with the effect of filler metals such as austenitic stainless steel, ferritic stainless steel and duplex stainless steel on tensi
An axisymmetrical unit cell model was used to represent a bimodal Al alloy that was composed of both nano-grained (NG) and coarse-grained (CG) aluminum. Effects
Nanocrystalline Cu with average grain size of 22.8-25.3 nm was prepared by vacuum-warm-compaction method. Scanning electronic microscope, HMV-2 type microhardne
The upconversion emission spectra of Er3+ doped oxyfluoride tellurite glasses excited by 808 nm laser diode (LD) were measured. The dependence of 550 nm upconve
The effects of Sb and Sr on the modification and refinement of Mg2Si phase in an AZ61-0.7Si magnesium alloy were investigated and compared. The results indicate
Precursive iron films with different grain sizes were prepared by magnetron sputtering on substrates heated at different temperatures. The iron films were sulfu