用2型试样和5型试样分别测试了J-0010薄膜的拉伸强度。5型试样测试结果的模式更有利于薄膜样品间拉伸强度的比较。对1#薄膜分别施以100、200、300、500mm/min的拉伸速度进行拉伸强度测试。实验结果表明,可以采用较高的拉伸速度进行薄膜拉伸强度的测试,以缩短实验周期。经过一系列实验,建立了适用于本实验的薄膜拉伸强度的测试方法。
Tensile strength of J-0010 film was tested with Type 2 and Type 5 specimens, respectively. The results of the Type 5 test patterns are more favorable for the comparison of the tensile strength between film samples. Tensile strength tests were performed on 1 # films at 100, 200, 300 and 500 mm / min, respectively. The experimental results show that the higher tensile speed can be used to test the film tensile strength to shorten the experimental period. After a series of experiments, the test method of tensile strength of the film suitable for this experiment was established.