论文部分内容阅读
Ni/ (10NiO-NiFe2O4 ) cermets were fabricated by using cold pressing-sintering method. The phase composition and effect of metallic content on the mechanical properties such as bending strength, Vickers hardness,fracture toughness and thermal shock resistance were studied. The results show that the cermets consist of Ni, NiO and NiFe2O4. Within the range of metallic content from 0 to 17% (mass fraction), the relative density decreases with the increase of metallic content and the decrease of sintering temperature, Vickers hardness decreases from 7 097 MPa to 4 814 MPa and the bending strength increases from 110 MPa to 157 MPa, and the fracture toughness mal shock testing falls sharply as the thermal shock temperature difference is above 200℃. The cermets samples,whose metallic content is 10% and 15%, respectively, exhibit promising property of thermal shock resistance at 960 ℃ with six cycles of heating and quenching testing.