The effect of cooling(laminar cooling)start temperature on the phase constitution was analyzed by quantitative metallography.The martensite/austenite(M/A)island distribution was fixed by colour metallography.The strength and uniform elongation of the steels were tested with quasi-static tensile testing machine.The in-coordinate deformation of the soft and hard phases was analyzed using FEM.The results indicate that when the cooling start temperature is 690 ℃,the mechanical properties are the best,meeting the requirements of X80 high deformability pipeline steel.
The effect of cooling (laminar cooling) start temperature on the phase constitution was analyzed by quantitative metallography. Martensite / austenite (M / A) island distribution was fixed by color metallography. Strength and uniform elongation of the steels were tested with quasi- static tensile testing machine. The in-coordinate deformation of the soft and hard phases was analyzed using FEM. The results indicate that when the cooling start temperature is 690 ℃, the mechanical properties are the best, meeting the requirements of X80 high deformability. pipeline steel .