【摘 要】
：
采用失重法,并结合物相分析技术研究了B2205、B409及B439不锈钢在700℃熔融LiCl-5 mass%Li_2O中的腐蚀行为.结果表明,三种不锈钢均遭受严重腐蚀,且其腐蚀失重近似遵循线性规
【机 构】
：
中国科学院金属研究所 金属腐蚀与防护国家重点实验室,
论文部分内容阅读
采用失重法,并结合物相分析技术研究了B2205、B409及B439不锈钢在700℃熔融LiCl-5 mass%Li_2O中的腐蚀行为.结果表明,三种不锈钢均遭受严重腐蚀,且其腐蚀失重近似遵循线性规律.不锈钢的腐蚀速率随其Cr含量的增加而减小.不锈钢的快速腐蚀与循环的氯化-氧化反应有关.同时,Li也能快速内扩散形成相应的含锂化物.
The corrosion behavior of B2205, B409 and B439 stainless steels in molten LiCl-5 mass% Li_2O at 700 ℃ was investigated by weight loss method and phase analysis technique.The results showed that all three stainless steels suffered severe corrosion and their corrosion weight loss approximated The linear rule is that the corrosion rate of stainless steel decreases with the increasing of Cr content.The rapid corrosion of stainless steel is related to the cyclic chlorination-oxidation reaction, while Li also diffuses rapidly to form the corresponding lithium-containing compound.
其他文献
随着我国科学技术的不断发展,单片机作为集成电路芯片,被广泛应用到各个领域,也使国家对于数字电路的学科教育逐渐受到重视。但是模拟电路的学科教学,会涉及编程,这就给技工
针对具有显著面内异性的钛合金TA2M板料,给出了材料厚向异性指数R值的三角函数分布规律, 在此基础上,基于势流原理和边界元法,提出了面内异性的钛合金板料在拉深成形中,凸缘
渤海大学辽宁沿海经济带发展研究院成立于2012年7月1日。研究院聚合渤海大学管理学、经济学、法学、社会学、教育学、历史学、马克思主义理论等相关学科科研资源,以辽宁沿海
摘要：结合鞍钢1580mm热轧带钢生产线，分析热轧板带钢的板形控制技术，以达到解决板形不良的问题的目的。 关键词：热轧带钢；板形；板形控制 中图分类号：TF3 文献标识码：A 文章编号：1671—7597（2012）0510153—01
A high power, intense current density electon beam was generated in the Pseudospark chamber filled with 15pa N_2 driven by a modified pulse line accelerator. Th
In 1995, we finished two nuclear model calculation programs CCRMN and OMHF, further improved the optical model parameters library, and made very significant pr
为获得高强耐蚀的镁稀土合金,采用扫描电镜、X射线衍射分析、腐蚀失重法、电化学阻抗和动电位极化等研究了元素Ce对Mg-9Gd-4Y-1Nd-0.6Zr合金微观组织和耐蚀性的影响。结果表
ＰｒｅｌｉｍｉｎａｒｙＳｔｕｄｙｏｆｔｈｅＧｉａｎｔＤｉｐｏｌｅＲｅｓｏｎａｎｃｅｉｎＨｏｔＲｏｔａｔｉｎｇＮｕｃｌｅｕｓ~（１３２）ＮｄＨｕａｎｇＺｈｅｎｇｄｅ；ＸｉａＨａｉｈｏｎｇ；ＨｏｕＬｏｎｇ；ＺｈｕＬｉｈｕａ；ＤｉｎｇＤａｚｈａｏＴｈｅｍｅ?..
Preliminary Study of the Giant Dipole Activation in Hot Rotating Nucleus ~ (132) NdHuang Zhengde; XiaHaihong; HouLong; ZhuLih
ＣｏｎｓｉｓｔｅｎｔＤｙｎａｍｉｃａｌａｎｄＳｔａｔｉｓｔｉｃａｌＤｅｓｃｒｉｐｔｉｏｎｏｆＦｉｓｓｉｏｎａｎｄＣｏｍｐａｒｉｓｏｎＷａｎｇＳｈｕｎｕａｎＷｉｔｈｉｎｔｈｅｆｒａｍｅｗｏｒｋｏｆｔｈｅＢｏｈｒｃｈａｎｎｅｌｔｈｅｏｒｙ，ａｎｄｔｈｅａ...
ConsistentDynamicalandStatisticalDescriptionofFissionandComparisonWangShunuanWithintheframeworkoftheBohrchanneltheory, andthe
采用相场方法模拟了Ti-Al-Nb合金α2→O相转变,探讨了有无外力场作用下弹性应变能对O相颗粒形貌、取向、数目、体积分数及平均尺寸的影响.结果表明:在弹性应变能作用下,颗粒