This paper introduces the research and development of high strength A517Q developed by Baosteel for platform rack,with micro-alloying adding suitable quenching and tempering process,trial thickness of 127 - 178 mm high-strength A517Q.The trial plate crossing thickness has a uniform mechanical properties, yield strength greater than 700 MPa,tensile strength than 790 MPa,the Charpy impact than 90 J at -40℃, aging impact than 69 J,has high strength and excellent low temperature impact toughness,While the plate has excellent resistance to crack tearing ability of low-temperature,NDT is less than -45℃.The Developing heavy plates had been used for manufacturing racks of 200-foot jack-up offshore platform,the performance meeting the requirements of the ABS,CCS classification societies.
This paper introduces the research and development of high strength A517Q developed by Baosteel for platform rack, with micro-alloying suitable for quenching and tempering process, trial thickness of 127 - 178 mm high-strength A517Q. The trial plate crossing thickness has a uniform mechanical properties, yield strength greater than 700 MPa, tensile strength than 790 MPa, the Charpy impact than 90 J at -40 ° C, aging impact than 69 J, has high strength and excellent low temperature impact toughness, While the plate has excellent resistance to crack tearing ability of low-temperature, NDT is less than -45 ℃. Developing Senior plates had been used for manufacturing racks of 200-foot jack-up offshore platform, the performance meeting the requirements of the ABS, CCS classification societies.