MoS2-decorated C3N4 (C3N4/MoS2) nanosheets hybrid photocatalysts were prepared by a simple sonication-impregnation method.Face-to-face lamellar heterojunctions were well established between two dimension (2D) C3N4 and MoS2 nanosheets.The effects of MoS2 c
【机 构】
：
School of Environmental and Chemical Engineering, Jiangsu University of Science and Technology, Zhen
【出 处】
：
武汉理工大学学报（材料科学版）（英文版）
论文部分内容阅读
MoS2-decorated C3N4 (C3N4/MoS2) nanosheets hybrid photocatalysts were prepared by a simple sonication-impregnation method.Face-to-face lamellar heterojunctions were well established between two dimension (2D) C3N4 and MoS2 nanosheets.The effects of MoS2 content on the light absorption,charge transfer and photocatalytic activity of the hybrid samples were investigated.Characterization results show that MoS2 nanosheets are well anchored on the face of C3N4 nanosheets and the composites have well dispersed layered morphology.After loading with MoS2,the light absorption of composites was much improved,especially in visible-light region.The photocatalytic activities of C3Na/MoS2 samples were evaluated based on the H2 evolution under visible light irradiation (λ ＞ 400 nm).When the loading amount of MoS2 was increased to 5 wt％,the highest H2 evolution rate (274 μmol·g-1·h-1) was obtained.Compared with samples obtained from direct impregnation method,sonication pretreatment is favorable for the formation of 2D layered heterojuctions and thus improve the photocatalytic activity.Slightly deactivation of C3N4/M oS2 composites could be observed when recycled due to the mild photocorrosion of MoS2.Based on the band alignments of C3N4 and MoS2,a possible photocatalytic mechanism was discussed,where MoS2 could efficiently promote the separation of the photogenerated carriers of C3N4.
其他文献
A molecular structural mechanics approach combining with finite element analysis (MSM/FEA) was applied to study the microstructure and tensile behaviors of bamboo-like carbon nanotubes (BCNTs).The mathematical model of tensile behaviors of BCNTs was estab
A facile deposition method has been developed for large-scale synthesis of visible-light-driven AgBr/montmorillonite composite catalyst for the first time.The as-synthesized samples were characterized by X-ray diffraction (XRD),X-ray photoelectron spectro
The regular distribution of micro-droplets splitting from thin ferrofluid layer is systematic experimentally investigated,as the layer is placed in a vertical magnetic field.In this work,the field is applied in an instant manner and a slow manner,respecti
Toxic Cu(Ⅱ) and Ni(Ⅱ) ions in aqueous solutions were adsorbed by microporous activated carbon (AC).The adsorption isotherm and kinetics correlation coefficients indicate that the adsorption of Cu(Ⅱ)and Ni(Ⅱ) ions on the AC fits the pseudo second-order rat
Magnesium ion-exchanged a-zirconium phosphates (Mg-a-ZrP) with particle sizes of 600 and 80 nm were prepared through the sealed ion-exchange and one-step hydrothermal synthesis methods,respectively.It was found that larger particles of Mg-a-ZrP had a high
To verify the effect of Al2O3 particle content and size as an abrasive on resin matrix friction materials for mining equipment,the tribological performance of friction materials was studied by using a block-on-ring tribotester over a wide range of applied
A series of heteropoly acid (HPA) based Al2O3 catalysts with three-dimensional ordered (3DOM) structure were synthesized by colloidal crystal template method. Interconnected macropores (250 nm) could be clearly observed by scanning electron microscope (SE
Ti,Al,graphite and diamond powders were used as raw materials to prepare Ti2AlC matrixbonded diamond composite using self-propagating high-temperature synthesis (SHS) method.The effect of diamond size and content on the fabrication of Ti2AlC-bonded diamon
A temperature stable Li2Zn0.95(SrxCa1-x)0.05Ti3O8 (0≤x≤1) ceramics were fabricated using a conventional solid-state route sintered at 1100 ℃ for 4 h. The XRD results indicate that the main phase Li2ZnTi3O8 and secondary phase including SrxCa1-xTiO3 (0≤x≤1
We reported a low cost, high efficiency hydrogen generation method from NaBH4 hydrolysis promoted by oxalic acid. NaBH4 and H2C2O4 were premixed and hydrogen generation was initiated by adding water into the solid mixture. H2C2O4 was selected as the acid