γ-Al2O3为低温型晶体,是尖晶石型结构,n(O)∶n(Al3+)为1∶2,在氧化气氛下升温至950~1000℃时,则向α-Al2O3转变.α-Al2O3中氧原子呈六方密堆积,Al3+离子仅占据氧八面体空隙.在氮气氛下,尖晶石结构在高温下可稳定存在...
γ-Al 2 O 3 is a low-temperature type crystal with a spinel structure. When n (O): n (Al 3+) is 1: 2, γ-Al 2 O 3 transitions to α-Al 2 O 3 when heated to 950-1000 ° C in an oxidizing atmosphere. The α-Al2O3 oxygen atoms hexagonal close packing, Al3 + ions only occupy the oxygen octahedral voids. Under nitrogen atmosphere, the spinel structure can stably exist at high temperature ...