Effects of surface states over core-shell Ni@SiO2 catalysts on catalytic partial oxidation of methan
【机 构】
:
College of Chemistry & Chemical Engineering, Taiyuan University of Technology, Taiyuan 030024, Shanx
【出 处】
:
能源化学
【发表日期】
:
2015年1期
其他文献
Enhanced electrochemical performance of Li-ion batteries with nanoporous titania as negative electro
The key point in CO2 methanation is to improve the activity at low temperature and the stability.For this purpose,a new cerium-modified Ni-La2O3/ZrO2 catalyst was prepared using La1-xCexNiO3/ZrO2 with perovskite phase as the precursor,which was obtained b
The cycle life of oxygen carrier (OC) is crucial to the practical applications of chemical looping combustion (CLC).Cycle performance of Cu/SiO2 prepared with a mechanical mixing method was evaluated based on a CLC process characterized with an added meth
A comparative study on different regeneration processes of Pt-Sn/γ-Al2O3 catalysts for propane dehyd
Three different regeneration processes including hydrogen or nitrogen purging and coke-burning treatment were used to restore the Pt-Sn/γ-Al2O3 catalysts,through which propane dehydrogenation reaction was performed in a consecutive reaction-regeneration m
CuZnAl catalysts with different La loadings were prepared by a complete liquid phase method and tested for higher alcohols (C2+OH) synthesis from syngas at the conditions of 250-290 ℃,4.SMPa,feed low rate=150mL/min and H2/CO=2.The catalysts were character
Ozone electrogeneration on Pt-TaOy sol-gel film modified titanium electrode: Effect of electrode com
Pt/WO3/C nanocomposite with parallel WO3 nanorods as cathode catalyst for proton exchange membrane f
Cellulose,the most abundant organic polymer on Earth,is a sustainable source of carbon to use as a negative electrode for sodium ion batteries.Here,hard carbons (HC) prepared by cellulose pyrolysis were investigated with varying pyrolysis temperature from
The matrix catalytic function when cracking the feed oil with large molecular size was systematically studied using three different catalyst configurations,including staged bed,partly mixed bed and completely mixed bed.Results showed that molecules in the
To date,most of the research on electrodes for lithium sulfur batteries has been focused on the nanostructured sulfur cathodes and achieves significant success.However,from the viewpoint of manufacturers,the nanostructured sulfur cathodes are not so promi