An annealed 50 Cr V4 steel was subjected to cyclic heat treatment process that consists of repeated short-duration(200 s)held at 840 °C(above Ac3 temperatu
Microstructure and mechanical properties of modified ultrahigh carbon(1.6%C)steels with different Mo additions(0,0.3%,0.5%,and 0.8%,mass fraction)were studied i
The dynamic recrystallization(DRX) process of hot compressed aluminium alloy 7050 was predicted using cellular automaton(CA) combined with topology deformation. The