【摘 要】
：
研究微胶囊红磷(MRP)和聚苯醚(PPO)复合阻燃剂对高抗冲聚苯乙烯(HIPA)材料力学性能的影响,并用抗冲击改性剂ABA及AEBA对高抗冲聚苯乙烯(HIPS)/微胶囊红磷(MRP)/聚苯醚(PPO)无
【机 构】
：
北京化工大学塑料机械及塑料工程研究所,
论文部分内容阅读
研究微胶囊红磷(MRP)和聚苯醚(PPO)复合阻燃剂对高抗冲聚苯乙烯(HIPA)材料力学性能的影响,并用抗冲击改性剂ABA及AEBA对高抗冲聚苯乙烯(HIPS)/微胶囊红磷(MRP)/聚苯醚(PPO)无卤阻燃材料的抗冲击性能和阻燃性能进行优化。结果表明:MRP和PPO的加入均会使HIPS体系的冲击性能下降,抗冲击改性剂ABA及AEBA的加入改善了无卤阻燃HIPS的悬臂梁冲击强度,且对材料的阻燃性没有影响,制得增韧改性后的无卤阻燃HIPA材料具有优异的阻燃和力学等综合性能。
The effects of MRP and PPO on the mechanical properties of high impact polystyrene (HIPA) were studied. The effects of high impact polystyrene (ABA) and AEBA The impact resistance and flame retardancy of HIPS / MRP / PPO halogen-free flame retardant materials are optimized. The results showed that both the addition of MRP and PPO decreased the impact properties of HIPS system. The addition of impact modifiers ABA and AEBA improved the Izod impact strength of HIPS without affecting the flame retardancy , The toughening-modified halogen-free flame retardant HIPA material has excellent comprehensive properties of flame retardancy and mechanics.
其他文献
刻画了2×2无界奇异∮-自伴算子矩阵的可逆性,并且得到相应的缺项算子矩阵存在可逆补的充分必要条件,最后举例验证了结果的合理性.
目的:建立接骨挫伤胶囊中士的宁的含量测定方法。方法:DIKMA C18色谱柱(4.6 mm×250 mm,5μm),流动相甲醇-水-冰醋酸-三乙胺(76∶230∶2.4∶0.3),检测波长254 nm,流速1.20 mL
摘要本文研究偶阶半线性中立型分布时滞微分方程,利用广义Riccati变换和积分平均技巧得到方程一切解均为振动的若干新的振动准则,推广和改进了一些文献中的结果.
介绍了单斜磷酸钒锂[ Li3 V2( PO4)3]的结构和充放电机理;综述了制备Li3 V2( PO4)3的方法,如高温固相法、溶胶-凝胶法和水热法的现状,以及改性,如表面包覆和元素掺杂等的进展
采用不同能量和剂量的N+离子束,对郑58、昌7-2和K12玉米自交系的干种子进行处理,结果表明,发芽率、发芽势和农艺性状变异都有很大差异,筛选出的N+离子束注入玉米自交系最佳诱
对鸡miR-18la的靶基因进行了预测及相关生物信息学分析,为深入研究miR-18la生物学功能提供理论指导.利用TargetScan 5.1与PicTar 2种计算方法对miR-18la进行靶基因预测,交集
采用固相法制备了钙钛矿型氧化物Sm0.5-xCdxSr0.5CoO3-δ(x =0,0.1,0.2,0.3,0.4,0.5)粉体.利用XRD分析材料的物相组成,用热膨胀仪测定了材料的热膨胀系数.利用交流阻抗法测试
本文研究了一个新的解析函数子类Mλ(g,h,ｕ,φ),(0≤λ≤1)的系数不等式.利用分析的方法和技巧,得到它精确的Fekete-Szeg(o)不等式及通过分式微分定义的函数类的Fekete-Szeg(o
通过高温固相法合成了Sr2 MgSi2O7:Eu2+,Nd3+发光材料,测试了样品的物相结构、可见和近红外激发和发射光谱、荧光寿命等,研究了Eu2+对Nd3+的近红外发光性能的影响及近红外发
利用掠入射X射线衍射法(GIXD)对PLLA和PHB混合制成的薄膜进行研究.通过改变两者的混合比、分子量、膜厚等参数,观察PHB的加入对混合薄膜中PLLA的结晶性的影响,并与相同条件下