The corrosion behavior and the effects of temperature on critical chloride content (Ccrit) of steel fibers in RPC were analyzed by a pH meter, ion chromatography, mercury intrusion porosimetry (MIP), and electrochemical techniques. It was found that the s
【机 构】
：
College of Civil and Resource Engineering, University of Science and Technology Beijing, Beijing 100
【出 处】
：
武汉理工大学学报（材料科学版）（英文版）
论文部分内容阅读
The corrosion behavior and the effects of temperature on critical chloride content (Ccrit) of steel fibers in RPC were analyzed by a pH meter, ion chromatography, mercury intrusion porosimetry (MIP), and electrochemical techniques. It was found that the suspension pH value, the chloride binding capacity, and the total porosity of RPC were lower than those of high-performance concrete (HPC). The pore structure of RPC mainly consisted of gel pores. The Ccrit values of steel fibers in RPC and HPC at 20 ℃ were 1％ and 2％, respectively. When the temperature reached 50 ℃, the Ccrit value of steel fibers in HPC decreased significantly, whereas it remained unchanged in RPC. The corrosion rate of corroded fibers in both RPC and HPC started to decrease with the rise in temperature.
其他文献
Fly ash (FA) was utilized to hydrothermally synthesize FA based Al-substituted tobermorites, and was combined with raw materials of FA and municipal solid waste incineration fly ash (MSWI) to hydrothermally synthesize FA-MSWI based Al-substituted tobermor
In order to reflect truly the damage evolution mechanism of weak muddy intercalation in dry-wet cycles, two typical weak muddy intercalations were selected for dry-wet cycles. The mineral changes of specimens were analyzed via X-ray diffraction after dry-
The bovine hydroxyapatite (BHA) was applied to prepare biological tissue engineering scaffolds by the method of extrusion freeforming.To achieve this goal,BHA were added to sodium alginate (SA) solution to form a slurry system in appropriate proportion.Th
Mg/Ni hybrid foams were fabricated by the electroless method. The Ni-P (Nickel-Phosphorous) coatings were deposited on the surface of closed-cell Mg alloy foams. The composition, microstructure and phases of the Ni-P coatings were characterized by scannin
Ti(C,N)-TiB2 cermets were fabricated from Ti(C,N), TiB2, Co and WC powder mixtures via a vacuum hot pressing process. The influence of TiB2 content on their microstructures and mechanical properties was investigated. As a result of the elevated TiB2 conte
A low-cost and efficient filter medium for Cd(II) removal was prepared by anchoring -SCN functional groups (by 3-thiocyanatopropyltriethoxysilane, TCPS) on ceramsite via the approach of synthesizing a honeycomb calciumaluminum-silicate-hydrate (C-A-S-H) l
An adhesive of the SiBCN ceramic was synthesized through the polymer derived ceramics (PDC) route. Meanwhile with higher adhesion strength and simpler process condition, the polyborosilazane (PSNB) was modified by E-44 epoxy resin. The E-44 epoxy resin wa
We developed cordierite-mullite composite ceramic materials to package and encapsulate PCM, and presented a preparation process from raw materials of kaolin, talc and alumina. The properties and microstructre of cordierite-mullite composite ceramic were s
Structure and mechanical properties of Calcium silicate hydrate (C-S-H) at a molecular level act as “DNA” of cement-based construction materials. In order to understand loading resistance capability of C-S-H gel, research on molecular dynamics (MD) was ca
A mild chemistry route was developed to prepare carbonaceous nanofibers-titanium dioxide (CNF-TiO2) nanocomposites for removal of dye pollutants. In the process of the template-directed hydrothermal carbonization (HTC), ultrathin Te nanowires were adopted