本发明是关于用混入气相防锈剂的粘合剂涂布了的合成树脂薄膜应用于黑色金属和有色金属防锈的方法。一般说来,不管哪一种金属零件,在加工前,都要对其施行除锈。过去,为了节省除锈时间,通常采取在未加工的金属上涂布防锈漆、防锈油、防锈涂料的方法。但是,采用涂布防锈油、防锈漆时,在生产过程中间或最后工序,都要脱脂清洗,设备费用大,不仅增加了处理工序、相当麻烦,而且生产成本增高。若采用防锈涂料,又必须对
The present invention relates to a method of applying a synthetic resin film coated with a binder mixed with a vapor-phase rust inhibitor to rust-preventing ferrous and non-ferrous metals. In general, no matter what kind of metal parts, before processing, should be carried out rust. In the past, in order to save the rust removal time, the method of coating anticorrosive paint, antirust oil and antirust paint on unprocessed metal is usually adopted. However, the use of anti-rust oil coating, anti-rust paint, in the middle of the production process or the final process, should be degreasing cleaning, equipment costs, not only increased processing steps, quite troublesome, but the cost of production increased. If using anti-rust paint, but also must