【摘 要】
：
In order to consume the Yellow River sediment as much as possible and improve the longterm stability of the Yellow River,Yellow River sediment was utilized as the main raw material to produce a composite material.Ca(OH)2 was used as alkali-activator to ac
【机 构】
：
Institute of Building Materials School of Civil Engineering, Dalian University of Technology, Dalian
【出 处】
：
武汉理工大学学报（材料科学版）（英文版）
论文部分内容阅读
In order to consume the Yellow River sediment as much as possible and improve the longterm stability of the Yellow River,Yellow River sediment was utilized as the main raw material to produce a composite material.Ca(OH)2 was used as alkali-activator to activate the active SiO2 and Al2O3 compositions in Yellow River sediment.10 wt％ slag was added into the mixture to further improve the strength of the composites.The effect of activity rate of the Yellow River sediment and dosage of Ca(OH)2 on the compressive strength of the Yellow River sediment-slag composite material at different curing ages was researched.XRD,SEM/EDS,light microscope and FTIR were used to further explore the products and the microstructure of the composite material.Results showed that the active ratio of sediment had a great influence on the compressive strength of specimen.In addition,the compressive strength of specimen increased with the increase of Ca(OH)2 dosage and curing age.When the dosage of Ca(OH) 2 was more than 5 wt％ as well as the curing age reached 90 days,the compressive strength of the composite material could meet the engineering requirement.In the alkali-activated process,the main product was hydrated calcium silicate (C-S-H) gel,which filled up the gaps among the sediment particles and decreased the porosity of the specimen.Moreover,the CaCO3 produced by the carbonization of the C-S-H gel and excess Ca(OH)2 also played a role on the strength.
其他文献
Influence of structural variations of N-vinylimidazolium tetrahalogenidoferrate (III) magnetic ionic liquids (MILs) on thermal properties was investigated. Using Gaussian09/B3PW91/6-311G (2d, p) density functional methods, the microstructure of the MILs w
To improve both oxygen evolution efficiency and stability at high temperatures,Mn,Mn+Mo,Mn+Mo+V,and Mn+Fe+V oxide electrodes were prepared on a Ti substrate,with an intermediate layer of IrO2,by an anodic deposition method.The crystal structure,surface mo
Different heating treatments with the variation of heating rates, holding temperatures and holding time were used to simulate the LTPS procedure. The experimental results show that the reheating shrinkage rates of glass substrates are rarely changed with
We fabricated the nanofiber composite membranes by impregnating Nafion into the modified polyvinylidene fluoride(PVDF) electrospinning nanofiber mat for proton exchange membrane fuel cells applications. The hydrophobic PVDF nanofibers mat became to the hy
To investigate the acoustic emission (AE) characteristics of quasi-brittle materials like rock and concrete, and to further analyze their damage and failure mechanism under seismic and other dynamic loads, the uniaxial tension test of granite cylinder spe
In order to develop high-performance diamond wheels, the vitrified bond with different contents of Li2O addition and corresponding diamond composites were prepared. The experimental results show that the addition of a small content of Li2O leads the forma
Influences of alkali oxides doping on the crystal structure,defects and hydration behavior of tricalcium silicate C3S were investigated by X-ray powder diffraction with the Rietveld method,inductively coupled plasma optical emission spectroscopy,thermolum
Slow positron beam was applied to study the depth profile structure of the virgin and the aged high-temperature vulcanized silicone rubber (HTV). Scanning electron microscope (SEM) images show that the surface of virgin sample is smooth, while the outdoor
The adventitious carbon located at 284.8 eV was used to calibrate samples without the carbon themselves. When the carbon is as a major part of the inorganic material, the adventitious carbon should be identified and used as the reference. There is no adve
Nanoparticles and microparticles reinforced Al matrix composites were fabricated by spark plasma sintering, and the microstructure and tribological properties were investigated systemically. The nano-Al2O3 particle and micro-Al2O3 particle uniformly dispe