【摘 要】
:
The effect of Zr content on exchange coupling and magnetization reversal of the Nd12.3Fe81.7-xZrxB6 (x=0-3.0) ribbons was systematically investigated.Interactio
【机 构】
:
State Key Laboratory for Advanced Metals and Materials
论文部分内容阅读
The effect of Zr content on exchange coupling and magnetization reversal of the Nd12.3Fe81.7-xZrxB6 (x=0-3.0) ribbons was systematically investigated.Interaction domains were imaged by magnetic force microscopy (MFM).The strength of interactions determined by Wohlfarth's analysis increased first with Zr content x increasing,reached the maximum value at x=1.5,and then decreased with x further increasing.Initial magnetization curves and dependence of coercivity and remanence on applied magnetic field showed that the mechanism of coercivity in all samples was mainly of exchange coupling pinning type,which was enhanced with x increasing.It was found by three-dimensional atom probe (3DAP) that Zr atoms did not partition into the Nd2Fe14B hard magnetic phase,but significantly enriched at the interfacial region.
其他文献
文章根据质量管理体系的要求,结合血站的行业特点及相关的法律法规的规定,对血站如何建立适宜的质量目标及质量目标的管理要求等内容进行探讨。
目的:对社区新发现的糖尿病患者进行分级管理,了解社区综合防治的效果。方法:从2008年起,按照《上海市社区糖尿病防治工作指南》的要求,对通过社区门诊、健康体检等途径发现的糖尿
在新形势下,我国卫生部出台了《医院会计制度》以及《医院财务制度》,该两项制度重点突出了成本管理,有效控制了财务风险,规范了核算程序,同时对提高医院财务管理水平起到了十分重
目的:探讨腔镜设备及腔镜精密手术器械的有效管理方法。方法:实行全员培训,固定专人管理,专人负责清洗腔镜精密手术器械,制定精密手术器械的清洗流程,设立腔镜质量控制小组,制定腔镜
目的:了解不同地区儿童视力状况,以便施行针对性措施挽救儿童视力。方法:对幼儿园及小学学生利用标准对数视力表(幼儿用儿童视力表)进行视力检查对有视力问题儿童再去医院进行详细
The effect of Sm-rich liquid phase (Sm2Co3) on magnetic properties and microstructure of 2:17-type Sm-Co magnet was studied.Three phases existed in liquid phase
Ho3+ doped glasses with various compositions xGeO2-(80-x)TeO2-9.5ZnF2-10NaF-0.5Ho2O3 (x=0,10,20,30,40,50,60,70 and 80) were prepared by a melt-quenching techniq
The anticorrosive properties of cerium based conversion coatings deposited on AA6061-T6 alloy by immersion in unbuffered cerium chloride and cerium nitrate solu
The new ternary YbZn0.7In1.3 compound was synthesized in evacuated quartz ampoules at 900 ℃,followed by annealing at 400 ℃.It crystallized in the UHg2 structu
Monodispersc (Sr,Eu)CO3 sphere (the homogenous mixture of Sr2+ and Eu3+ carbonates) was firstly prepared,and then its surface was coated by amorphous SiO2 in th