【摘 要】
:
采用等离子喷涂技术制备纳米结构氧化锆陶瓷涂层,通过扫描电镜观察发现涂层中存在两种相,即熔化相和未熔相,利用定量金相分析法计算两相的含量。在统计分析的基础上,研究了纳
【机 构】
:
桂林航天工业高等专科学校机械工程系,福州大学材料科学与工程学院,
论文部分内容阅读
采用等离子喷涂技术制备纳米结构氧化锆陶瓷涂层,通过扫描电镜观察发现涂层中存在两种相,即熔化相和未熔相,利用定量金相分析法计算两相的含量。在统计分析的基础上,研究了纳米氧化锆涂层断面的Vickers显微硬度。从硬度分布的Weibull图中可以看出,纳米氧化锆涂层的显微硬度存在双态分布,与涂层的两相组织一致。
The nanostructured zirconia ceramic coatings were prepared by plasma spray technique. Two phases were observed in the coatings by scanning electron microscopy, that is, the melting phase and the unmelted phase. The content of two phases was calculated by quantitative metallographic analysis. Based on the statistical analysis, the Vickers microhardness of the cross section of the nano-zirconia coating was studied. It can be seen from the Weibull chart of the hardness distribution that the microhardness of the nano-zirconia coating has a bimodal distribution consistent with the two-phase structure of the coating.
其他文献
肤色特征在MPEG4、基于内容的图像检索、虚拟现实等领域有着广泛的应用.目前肤色聚类的方法有很多,结果各异,但都没有涉及颜色现象的本质.探讨了人体肤色的基本问题:影响肤色
研究了淬火温度对25MnV钢组织及性能的影响。结果表明:在实验温度范围内,25MnV钢的强度、硬度先随淬火温度的升高而增加,在910℃时达到峰值,随后随淬火温度的升高而降低;25Mn
目的观察美沙拉嗪口服联合中药灌肠治疗溃疡性结肠炎的临床疗效。方法 65例患者随机分为治疗组35例,用美沙拉嗪口服联合中药保留灌肠,对照组30例用SASP口服及保留灌肠,观察两
通过化学镀方法在钢表面获得了镍-磷-金刚石复合膜,并对镀有复合膜的钢进行淬火及回火热处理,研究了淬火温度(450、650、850℃)和回火温度(200℃)对复合膜组织和性能的影响。
利用高精度差分膨胀仪,通过对20MnSi螺纹钢线膨胀行为的测量与分析,获得相关动力学信息,系统研究了不同淬火温度(900~600℃)下20MnSi螺纹钢冷却过程中的相变行为。结果表明:淬
在分析齿轮挤压凸模失效原因的基础上,通过调整凸模热处理工艺,延长了齿轮挤压凸模的使用寿命。
On the basis of analyzing the cause of the failure of the gear extrusi
采用有限元法中的电磁-热耦合技术,研究了中厚板感应回火加热中三维温度场的变化规律。结果表明:感应加热工艺参数对中厚板厚度、宽度方向的温差以及加热时间都有明显影响。
通过拉伸、冲击和断裂韧性等力学试验方法以及扫描电镜对低合金超高强度钢30Cr3SiNiMoV的力学性能和组织进行了研究,并采用热力学平衡计算(Thermo-Calc软件)方法,得到该钢的
对20Cr3MoWVA合金钢齿轮进行不同工艺的热处理,并对热处理后的金相组织、表面硬度和心部硬度进行检测分析。结果表明,20Cr3MoWVA钢齿轮经碳氮共渗或渗碳后,重新加热到910℃快
目的:评价我院2014年骨科Ⅰ类切口手术围手术期预防使用抗菌药物合理性,为加强抗菌药物临床应用管理提供参考。方法:回顾性分析我院2014年1-6月骨科Ⅰ类切口手术患者围手术期