The slag formation path is important for efficient dephosphorization in steelmaking processes. The phosphorus capacity and the melting properties of the slag are critical parameters for optimizing the slag formation path. Regarding these two factors, the phosphorus partition ratio was calculated using the regular solution model(RSM), whereas the liquidus diagrams of the slag systems were estimated using the FactS age thermodynamic package. A slag formation path that satisfies the different requirements of dephosphorization at different stages of dephosphorization in a converter was thus established through a combination of these two aspects. The composition of the initial slag was considered to be approximately 15wt%CaO –44wt%SiO 2–41wt%FeO. During the dephosphorization process, a slag formation path that follows a high-iron route would facilitate efficient dephosphorization. The composition of the final dephosphorization slag should be approximately 53wt%CaO –25.5wt%SiO 2–21.5wt%FeO. The composition of the final solid slag after dephosphorization is approximately 63.6wt%CaO –30.3wt%SiO 2–6.1wt%FeO. The phosphorus capacity and the melting properties of the slag are critical parameters for optimizing the slag formation path. Regarding these two factors, the phosphorus partition ratio was optimized using the regular solution model ( RSM), the liquidus diagrams of the slag systems were estimated using the FactS age thermodynamic package. A slag formation path that satisfies the different requirements of dephosphorization at different stages of dephosphorization in a converter was thus established through a combination of these two aspects. The composition of the initial slag was considered to be about 15 wt% CaO -44 wt% SiO 2-41 wt% FeO. The composition of the final dephosphorization slag should be about 53 wt% CaO-25.5 wt% SiO 2-21.5 wt% FeO. The composition of the final solid slag after dephosphorization is approximately 63.6 wt% CaO -30.3 wt% SiO 2-6.1 wt% FeO.