研究了直流磁控溅射法制备的Ni81Fe19/Cr82Al18 双层膜中的交换耦合.样品的室温矫顽力与1/t3/2FM(tFM为铁磁层厚度) 近似成正比例关系,从而表明在Ni81Fe19/Cr82Al18 中交换耦合为铁磁/ 反铁磁界面的随机相互作用.另外还讨论了反铁磁层厚度对交换偏置的影响.
The exchange coupling in Ni81Fe19 / Cr82Al18 bilayers prepared by DC magnetron sputtering was studied. The room temperature coercivity of the sample is approximately proportional to 1 / t3 / 2FM (tFM is the thickness of the ferromagnetic layer), indicating a random interaction of exchange coupling as ferromagnetic / antiferromagnetic interface in Ni81Fe19 / Cr82Al18. The effect of anti-ferromagnetic layer thickness on the switching bias is also discussed.