To alleviate the main limitations of lithium ion diffusion rate and poor electronic conductivity for LiFePO4 cathode material, it is desirable to synthesize nano-size LiFePO4 material due to its enhanced electronic and lithium ion transport rates and thus an improved high-rate performance. However, our previous synthesized LiFePO4 nanorods only exhibited low high-rate and slightly unstable cycle performance. Possible reasons are the poor crystallization and Fe2+ oxidation of LiFePO4 nanorods prepared by hydrothermal method. In this paper, LiFePO4 nanorods were simply dealt with at 700 ℃ for 4 h under the protection of Ar and H2 mixture gas. The electrochemical properties of LiFePO4/Li cells were investigated by galvanostatic test and cyclic voltammetry(CV). The experimental results indicated that the annealed LiFePO4 nanorods delivered an excellent cycling stability and obviously improved capacity of 150 mA·h·g-1 at 1C, and even 122 mA·h·g-1 at 5C.
To alleviate the main limitations of lithium ion diffusion rate and poor electronic conductivity for LiFePO4 cathode material, it is desirable to synthesize nano-size LiFePO4 material due to its enhanced electronic and lithium ion transport rates and therefore an improved high-rate performance. However, The previous reasons for the poor crystallization and Fe2 + oxidation of LiFePO4 nanorods prepared by hydrothermal method. In this paper, LiFePO4 nanorods were simply dealt with at 700 ℃ for 4 h under the protection of Ar and H2 mixture gas. The electrochemical properties of LiFePO4 / Li cells were investigated by galvanostatic test and cyclic voltammetry (CV). The experimental results indicated that the annealed LiFePO4 nanorods delivered an excellent cycling stability and obviously improved capacity of 150 mA · h · g-1 at 1C, and even 122 mA · h · g-1 at 5C.