【摘 要】
：
铜—石墨材料广泛用于高速滑动条件下工作的摩擦部件(如滑动电触头等)。本文所研究的铜-石墨材料,是用-1铜粉和C-1胶体石墨配成混合料,用双向压制成压坯,然后在950℃的氢气
论文部分内容阅读
铜—石墨材料广泛用于高速滑动条件下工作的摩擦部件(如滑动电触头等)。本文所研究的铜-石墨材料,是用-1铜粉和C-1胶体石墨配成混合料,用双向压制成压坯,然后在950℃的氢气介质中烧结2h得到试样,再进行精整,在某些情况下,还在450℃的温度下对其退火1h。然后测量其硬度、冲击韧性、横向抗弯强度和抗压强度。抗压试验的试样尺寸为:直径×高=10×15mm。
Copper - graphite materials are widely used in high-speed sliding friction parts work conditions (such as sliding electrical contacts, etc.). The copper-graphite material studied in this paper is compounded with -1 copper powder and C-1 colloidal graphite, pressed in two-way into compacts and then sintered in a hydrogen atmosphere at 950 ℃ for 2h to obtain a sample, In total, in some cases, it is also annealed at a temperature of 450 ° C for 1 hour. Then its hardness, impact toughness, transverse flexural strength and compressive strength were measured. The compression test specimen size: diameter × height = 10 × 15mm.
其他文献
本文评述了我国稀土中间合金生产工艺的发展历程和现状;简述了稀土中间合合冶炼过程的物理化学反应;通过对现行工艺存在问题的分析,指明了我国稀土中间合金的发展方向。
Thi
本文较系统全面地总结了国内外铁水预处理的研究和试验情况。并结合国内的实际情况,讨论了开展这项试验研究工作的意义和技术问题。 文中讨论了铁水预脱硅的方法,脱硅剂种类
目的:研究HSV-tk/GCV系统对小鼠肝癌细胞的体外杀伤作用.方法:利用重组DNA技术,将HSV-tk基因亚克隆至逆转录病毒载体(pLNCTK)中,在LipofectAMINE介导下,转染PA317包装细胞,G4
通过对液氮冷冻植骨治疗胫骨上端骨巨细胞瘤的研究，发现导致术后感染的原因。在３７例中，有７例感染，３０例非感染，其中前内侧切口占有率，感染组中有５例，非感染组中有６例，卡方检验，Ｐ值＜００５，提示前内侧
叙述我国金属制品行业对润滑剂的需求情况及国内市场供应现状,介绍我国金属制品企业、高等院校、科研单位和润滑剂生产厂为适应引进的高速拉丝机对润滑剂的需要,在消化吸收、
高强度钽钨合金Ta-10W、Ta-7.5W及Ta-2.5W等在化学工业中已有广泛应用。最近美国卡伯特公司KBI子公司又研制成功一种新的钽铌钨钼合金41合金(58 Ta 2Mo2.5W 37.5 Nb),该合金
癌症登记报告制度是开展恶性肿瘤防治研究工作的一项基本建设，它对制定肿瘤防治规划、考核防治措施、探讨肿瘤流行规律、研究肿瘤病因具有重要意义。癌症登记还可带动癌症病因
经营项目:(1)遮阳网(本公司生产的遮阳网保证使用3年以上);遮光率:30%、40%、50%、60%、70%、80%、90%;幅宽1.5～10.0m。(2)防虫网(本公司生产的防虫网保证使用3年以上);目数:2
空心电极是矿热炉上采用的新技术之一,目前已在电石、炼铁等生产工艺中应用。采用这项技术可降低电极消耗、提高原料利用率、提高电效率、节省电能。本文介绍了空心电极的发
根据连铸不锈钢的特点,研究了Cr_2O_3、TiO_2、B_2O_3对保护渣粘度和半球点温度的影响,并从理论上给予解释。
According to the characteristics of continuous casting sta