To evaluate the effect of actual cooling rate of liquid steel in the ladle on the metallurgical performances of a tundish,a transient and coupled computational model was developed to reveal the flow fields,temperature fields,residence time distribution of the molten steel and the inclusion removal efficiency in a typical single-strand tundish with given geometry and process parameters.The results showed that,with the decrease of the ladle stream cooling rate,the temperature difference of bulk flow at the outlet of tundish over a normal casting period decreased from11.3 to 2.6K,and the dead volume fraction of the tundish decreased from 17.58% to 14.35%,while the inclusion removal efficiency was increased especially for the inclusions with the diameter less than 50μm,whose removal ratio could be increased by 20.62%.When the cooling rate was less than 0.3K·min-1,however,the variation rates of the three evaluation criterions above declined significantly,which suggested that a critical value existed for the effect of the cooling rate of ladle stream on the tundish performances.The establishment of the critical ladle stream cooling rate should be very important to achieve persistent metallurgical properties of tundish over the whole casting stage,together with the reasonable ladle insulation design.
To evaluate the effect of actual cooling rate of liquid steel in the ladle on the metallurgical performances of a tundish, a transient and coupled computational model was developed to reveal the flow fields, temperature fields, residence time distribution of the molten steel and inclusion warning efficiency in a typical single-strand tundish with given geometry and process parameters. The results showed that, with the decrease of the ladle stream cooling rate, the temperature difference of bulk flow at the outlet of tundish over a normal casting period decreased from 11.3 to 2.6K, and the dead volume fraction of the tundish decreased from 17.58% to 14.35%, while the inclusion removal efficiency was increased especially for the inclusions with the diameter less than 50μm, whose removal ratio could be increased by 20.62% .When the cooling rate was less than 0.3K · min-1, however, the variation rates of the three evaluation criterions above declined significantly, which suggested that a critical va lue existed for the effect of the cooling rate of ladle stream on the tundish performances.The establishment of the critical ladle stream cooling rate should be very important to achieve persistent metallurgical properties of tundish over the whole casting stage, together with the reasonable ladle insulation design .