【摘 要】
:
Intermetallic compounds(IMC) formed at Sn-Ag-Cu solder droplet/pad interface during wetting reaction were investigated.Comparative studies of the IMC evolution
【机 构】
:
Microjoining Laboratory
论文部分内容阅读
Intermetallic compounds(IMC) formed at Sn-Ag-Cu solder droplet/pad interface during wetting reaction were investigated.Comparative studies of the IMC evolution during reflow and aging were also conducted. The results show that the wetting reaction between molten solder droplet and pad leads to the formation of Au-Sn compound at interface, but Au element is not fully consumed during wetting reaction. After reflow, all Au layer disappears from the interface, Au element is dissolved into solder and Au-Sn intermetallic compounds are precipitated in the bulk. Reaction between Ni layer and Sn-Ag-Cu solder leads to the formation of (CuxNi1-x)6Sn5 layer at interface during reflow. According to the thermodynamic-kinetic of interfacial reaction, the wetting reaction at solder droplet/pad interface influences the phase selectivity of IMC evolution during reflow and aging process.
其他文献
The extrusion of Al-Si alloy powders with different particle sizes allows manufacture of different products with unique microstructures and therefore with uniqu
The MoSi2 coating on C103 niobium based alloy was prepared by pack cementation method. The formative mechanism,morphology and structure of coating were investig
The room-temperature oxygen plasma treatment before depositing ZnO films on nanocrystalline diamond substrates was studied. The nanocrystalline diamond substrat
The effect of Nb in (La0.5Ce0.5)64-xAl16Ni5Cu15Nbx (x=0-5, mole fraction) bulk metallic glasses was investigated by X-ray diffractometry, differential scanning
In order to evaluate the effect of stoichiometric ratio upon electrochemical properties of AB5-type hydrogen storage alloys, a series of alloys Mm0.8La0.2(Ni4.0
The deformation behavior of squeeze cast ZK60 magnesium alloy was investigated by compressive tests conducted at temperatures of 250-450 ℃ and strain rates of
The effects of reactive gas partial pressure on droplet formation,deposition rate and change of preferred orientation of CrN and Cr2O3 coatings were studied. Fo
Many factors were found to have effects on the conversion coatings for AZ31 alloy, alloy the most important one in producing high quality conversion coatings is
The 7××× aluminum alloys having a microstructure with precipitate free zones (PFZ) nearby the grain boundary, have received a great deal of attention due to
The photoconductive characteristic of the inorganic/organic hybridized polymer system is reported,in which a novel bi-functional photorefractive (PR) poly(N-vin