The microstructure evolution of an extruded Mg-8.57Gd-3.72Y-0.54Zr (mass fraction,%,GW94) alloy during reheating into the semisolid state was investigated using
A method to reach the globular weld structure of A356 aluminum alloy using stirring the localized semisolid zone during butt-joining is developed.Since the heat