【摘 要】
：
选择自制的MU5和MU15可发性聚苯乙烯(简称EPS)轻质、节能混凝土砌块与多种级别的专用砂浆、普通砂浆配合,制作纯剪构件,开展EPS砌块砌体受剪破坏试验,观测砌体受力过程和变形
论文部分内容阅读
选择自制的MU5和MU15可发性聚苯乙烯(简称EPS)轻质、节能混凝土砌块与多种级别的专用砂浆、普通砂浆配合,制作纯剪构件,开展EPS砌块砌体受剪破坏试验,观测砌体受力过程和变形特点,以此分析EPS混凝土砌块砌体受剪性能,并通过分析整理实验数据,提出EPS轻质节能混凝土砌块砌体的抗剪强度计算公式.为该新材料的推广使用提供可靠的理论和实验指导.
Choose homemade MU5 and MU15 expandable polystyrene (EPS) lightweight, energy-saving concrete block with a variety of levels of special mortar, ordinary mortar, making pure shear components, carry out EPS block masonry shear failure test , To observe the process and deformation characteristics of masonry, so as to analyze the shear performance of EPS concrete block masonry, and to calculate the shear strength of EPS lightweight energy-saving concrete masonry by analyzing and sorting the experimental data. The promotion of new materials to provide reliable theoretical and experimental guidance.
其他文献
为探明叉车在偏载状态工作时,门架系统中左右起升液压缸的作用力是否均等,以某叉车中门架为例,运用Hyper Works软件,采用2种不同的边界条件进行有限元分析,分别模拟左右作用力均等和作用力不等2种情况;并对该门架进行应力应变电测试验,再将有限元分析结果与测试结果进行对比,得出结论:左右作用力不等的方案更接近电测试验结果,即叉车门架系统在偏载状态工作中左右起升液压缸作用力不等,为叉车门架系统的分析
山东省综合农业区划工作1983年开始,在利用1980年年报统计资料的基础上进行补充调查,综合分析,于1981年5月完成。1983年12月通过技术鉴定,1984年获省科技成果二等奖。 该项成
目的：比较经尿道前列腺等离子电切术（TUBVP）和经尿道前列腺电切术（TURP）治疗高龄良性前列腺增生的临床效果。方法选取2012年5月-2013年12月于本院诊治的良性前列腺增生高龄患者共7
目的探讨经超声引导下注入无水乙醇及顺铂治疗卵巢巧克力囊肿的临床效果。方法选择本院2012年5月~2013年7月收治的60例卵巢巧克力囊肿患者作为研究对象,将其随机分为对照组与
针对车道线检测算法计算量大,耗时长的问题,为提高算法的实时性和鲁棒性,把通过CCD获取的道路图像由视频转码模块TVP5158从模拟信号转化为数字信号,在进行工作区域的限定的基础上,进行灰度化,并利用改进的滤波算子进行图像的滤波处理;为利于后续步骤的处理,然后利用对噪声的低敏感性和更有利边缘的显示的Sobel算子进行边缘分割;然后在搭建DSP硬件平台上,结合改进的Hough算法,提高检测与识别的准确
目的探讨孕妇先兆流产影响因素与妊娠结局的关系。方法选取2014年1月~2015年1月我院门诊诊治的先兆流产孕妇80例,将其按妊娠结局的不同进行分组,研究组为妊娠结局良好的孕妇,
摘 要：为研究不同长度及直径的剑麻纤维对C40自密实轻骨料混凝土工作性能和力学性能的影响，通过对混凝土的坍落扩展度，T500，抗压强度及劈裂抗拉强度进行试验后发现：剑麻纤维长度和直径的变化对自密实轻骨料混凝土的抗压强度提高幅度很小，均在4.6%之内；随着剑麻纤维长度增加，抗拉强度均有较明显的提高，并呈现先升后降的规律；随着剑麻纤维直径增大，抗拉强度均有较大的增长，并呈现逐渐增大的趋势；随着剑麻纤维
近年来,随着日元不断升值,日本东京电力公司(以下简称东电)的设备采购比重已大幅度由国内扩展到了国外。只要价格便宜、质量上乘、企业信誉可靠,并经审核认可后,国外各公司均