以六水硝酸铈和甘氨酸为原料,聚乙二醇20000为分散剂,采用燃烧法一步合成了纳米二氧化铈粉体。通过对产物进行TG-DTA、XRD和TEM表征,讨论了原料配比,点火温度等因素对产物的
【机 构】
：
辽宁石油化工大学化学与材料科学学院,
论文部分内容阅读
以六水硝酸铈和甘氨酸为原料,聚乙二醇20000为分散剂,采用燃烧法一步合成了纳米二氧化铈粉体。通过对产物进行TG-DTA、XRD和TEM表征,讨论了原料配比,点火温度等因素对产物的影响。结果表明,反应的最佳温度为350℃,溶液的pH值为5,六水硝酸铈和甘氨酸(Gly)的摩尔比为1∶1.6,得到的产物的平均粒径为6.5 nm。
Using cerium nitrate hexahydrate and glycine as raw materials and polyethylene glycol 20000 as dispersant, the nano-sized ceria powder was synthesized by combustion method. The products were characterized by TG-DTA, XRD and TEM. The effects of the ratio of raw materials, ignition temperature and other factors on the products were discussed. The results showed that the optimum reaction temperature was 350 ℃, the pH value of the solution was 5, the molar ratio of cerium nitrate and glycine hexahydrate was 1: 1.6, and the average particle size of the obtained product was 6.5 nm.
其他文献
砼作为建筑工程施工中的重要材料,其质量问题直接影响到整个建筑工程的施工质量,尤其是砼工程在现代化建筑产业中越来越普遍,砼质量问题甚至成了影响整个建筑产业快速健康发
副主任医师:本病例为慢性肺心病并发感染急性发作,现请实习医师报告病历。实习医师:患者女,50岁。因慢支20年,肺心病8年,神志恍惚2天,于1985年10月9日第三次入院。二十年来,
本文报导了一例30岁加拿大妇女因两次发作全身性抽搐和持续性头疼、恶心、呕吐,于1979年12月入院。体检未见异常,神经外科检查未见感觉和运动障碍,实验室检查嗜酸粒细胞略有
今年6月17～24日,总后卫生部在石家庄召开了全军整顿药品制剂工作座谈会。总后卫生部卢乃禾副部长在会议开始时讲了话,北京军区后勤部、卫生部和河北省军区的领导同志参加了开
脱屑性间质肺炎(DIP)不论在成人及小儿均不多见。病理上此病的2个特征是沿肺泡腔细胞增生和是有充满肺泡腔的脱屑细胞,增生细胞是Ⅱ型肺泡上皮细胞,肺泡腔内非排列性细胞主
特发性弥漫性肺间质纤维化症,是一种严重的呼吸系疾病。国内文献只有零星报道,系统尸体解剖报告更少。我们将最近遇到的1例尸解病例报告如下,供同道们参考。病历摘要:患者,
为了解常规临床工作中短程化疗采用的程度,于英格兰及威尔士对1978年10月1日—1979年8月31日新登记初治肺结核病人进行调查,对象为2,390名15岁及以上有呼吸系病变者,治疗前
铜火法精炼工艺自问世以来,一直采用传统氧化还原法,主要缺点是氧化和还原是对立作业过程,其生产效率低,能耗高,黑烟污染严重。金隆铜业有限公司打破了传统氧化还原理论,创造
以往人们对直接穿刺颈段脊髓造影术后病人采取卧床24小时。作者对120例造影后病人随机地分为卧床24小时和完全自由活动两组进行对比观察。全部病人都经第一、二颈椎水平穿刺
《语文课程标准》(实验稿)把“努力建设开放而有活力的语文课程”作为课程基本理念之一。这一理念要求我们语文教学要创设开放而有活力的教学模式,创建这一模式要求实现教师