The parameters for the electro-deposition of Cu were optimized in order to increase the compressive properties of close cell aluminum. Different values of deposition voltages and times were considered to vary the amount of deposited Cu. The surface morpho
【机 构】
：
School of Material Science and Engineering, Chang’an University, Xi’an 710064, China;Key Laboratory
【出 处】
：
武汉理工大学学报（材料科学版）（英文版）
论文部分内容阅读
The parameters for the electro-deposition of Cu were optimized in order to increase the compressive properties of close cell aluminum. Different values of deposition voltages and times were considered to vary the amount of deposited Cu. The surface morphology of the coating was observed by SEM and the compressive properties were evaluated by MTS. The results show that the coating is more homogeneous and compact with increasing voltage in a certain range, and beyond which, the coating quality decreases apparently. The reason is dedicated to the discharge rate of Cu2+ and nucleus formed in unit time. The compression results show three experienced stages: elastic deformation stage, collapse deformation stage and densification stage. After the electro-deposition of Cu, the elasticity modulus is increased obviously and the platform stress is also increased. Under the same strain, the stress of the aluminum foam with coating is reinforced comparing with the aluminum foam without coating. Furthermore, the platform area is widened apparently. In addition, Cu-SiC nanocomposite coatings are electrodeposited in alumium foams for further improving the mechanical characterization.
其他文献
Through finite element numerical simulation and based on laminated plate theory, the effect of dimension on the torsion properties of uniform C/SiC composites pipe was studied to provide a theoretical guidance for preparing the C/SiC pipe with different d
The effect of strains on the thermal conductivity of Si/Ge superlattices was investigated by nonequilibrium molecular dynamics(NEMD)simulation.The thermal conductivities experienced a near linear drop with increasing tensile and compressive strains.It was
Bi2Te2.7Se0.3/Cu core/shell powders were prepared by electroless plating and hydrogen reduction,and then sintered into bulk by spark plasma sintering in order to improve the thermoelectric and mechanical properties of n-type Bi-Te thermoelectric material.
Photocatalytic reduction of CO2 was carried out on villiform spherical catalysts of Pd-TiO2 in isopropanol solution.The catalysts were synthesized by hydrothermal method,their structures,morphologies and optical absorption properties were characterized by
Manganese-doped Ba 0.925 Ca 0.075 TiO3 lead-free piezoelectric ceramics(abbreviated as BCT)with high mechanical quality factor were synthesized by conventional solid-state reaction method.The effects of excess Ba on the crystal structure,microstructure,an
Particle removal mechanism was presented during machining particle SiC/Al composites with diamond grinding tool. The relevant removal modes and their mechanisms were discussed considering the impact and squeezing effect of diamond grit on the SiC particle
The electron paramagnetic resonance (EPR) spectra of trigonal Mn2+ centers in Zn(ClO4)2·6(H2O) and Mg(ClO4)2·6(H2O) crystals were studied on the basis of the complete energy matrices for a d5 configuration ion in a trigonal ligand field. It was demonstrat
Nano hafnium carbide (HfC) powders were synthesized by sol-gel combining hightemperature rapid heat treatment process using citric acid and hafnium tetrachloride as the raw materials. The effects of ball milling treatment on the phase and morphology of py
Three-dimensionally ordered (3DOM) macroporous phosphotungstic acid/SiO2 (HPW/SiO2) materials were prepared by using colloidal crystal as templates and applied for oxidative desulfurization (ODS) of the model fuel oil. The obtained HPW/SiO2 materials were
To understand the enhancing effect and fiber-reinforced mechanism of composite fibers reinforced cement concrete, the influences of composite fibers on micro-cracks and the distribution of composite fibers were evaluated by optical electron micrometer (OE