【摘 要】
:
In order to prevent carbon/carbon composites from oxidation at 1873 K, an efficient oxidation protective SiC/Si-W-Mo coating was prepared by a two-step pack cem
【出 处】
:
Journal of University of Science and Technology Beijing
论文部分内容阅读
In order to prevent carbon/carbon composites from oxidation at 1873 K, an efficient oxidation protective SiC/Si-W-Mo coating was prepared by a two-step pack cementation technique. The microstructures and the phase composition of the as-received multi-coating were examined by scanning electron microscopy (SEM) and X-ray diffraction (XRD). It is seen that the compact multi-coating is composed of α-SiC, Si, and (WxMo1-x)Si2. Oxidation test shows that, after oxidation at 1873 K in air for 102 h and thermal cycling between 1873 K and room temperature for 10 times, the weight loss of the SiC/Si-W-Mo coated C/C composites is only 0.26%. The invalidation of the multi-coating is attributed to the formation of penetrable cracks in the coating.
In order to prevent carbon / carbon composites from oxidation at 1873 K, an efficient oxidation coating SiC / Si-W-Mo coating was prepared by a two-step pack cementation technique. The microstructures and the phase composition of the as-received multi- Coating was examined by scanning electron microscopy (SEM) and X-ray diffraction (XRD). It is seen that the compact multi-coating is composed of α-SiC, Si, and (WxMo1- after oxidation at 1873 K in air for 102 h and thermal cycling between 1873 K and room temperature for 10 times, the weight loss of the SiC / Si-W-Mo coated C / C composites was only 0.26%. The Invalidation of the multi -coating is attributed to the formation of penetrable cracks in the coating.
其他文献
Support Vector Machine (SVM) is a machine learning algorithm based on the Statistical Learning Theory (SLT), which can get good classification effects with a fe
A new hydrometallurgical process for a carbonaceous refractory gold concentrate at ambient temperature and pressure was presented, including grinding-leaching,
Calcium magnesium chlorosilicate doped by europium, Ca8Mg(SiO4)4Cl2:Eu2+, was prepared by the solid state reaction at high temperature. The compound obtained is
Barium strontium titanate/magnesia (BSTO/MgO) ferroelectric materials for phase shift were prepared by traditional ceramic process-solid phase synthesis. The ef
Fine and coarse aggregates play an important role in the fracture of concrete. However, quantitative information available on the effect of the coarse aggregate
Brittle-to-ductile transition (BDT) behavior and creep behavior of extruded NiAl-25Cr alloy at elevated temperatures were investigated. The results reveal that
This paper briefly reviews other peoples works on negative selection algorithm and their shortcomings. With a view to the real problem to be solved, authors bri
The surface tension of molten tin was determined by a set of self-developed digital equipment with sessile drop method at oxygen partial pressure of 1.0 × 10-6
The base structure of in situ TiCP/Fe composites fabricated under industrial condition was changed by different heat treatments. Erosive wear tests were carried
A novel soluble π-conjugated polymer, poly [(3-acetylpyrrole-2, 5-diyl) p-(N, N-dimethylamino) azobenzylidene] (PAPDMAABE), was synthesized by condensation of