论文部分内容阅读
The nanocrystalline La1-xSrxCrO3 was prepared by sol-gel method using La( NO3 )3 · 6H2O, Sr( NO3 )2 and respectively. The phase transformation from dry-gel to crystal was investigated by means of TG, DSC and XRD. Influences of temperature and Sr quantity on particle-diameters were observed by HREM. The experimental results show that the best calcined temperature is near 800 ℃. The particle-diameters decrease with the increase of Sr quantity. The chromite phase formed continuously during crystallization process, which is mainly composed of four steps: ( 1 ) Carbonates first formed by decomposing metal citrates. (2) The decomposition of carbonates occurred metal oxides. (3) La0. 9Sr0.1 CrO4 were synthesized by the reaction of metal oxides. (4) Chromite phase formed lastly due to the decomposition of chromate phase.