【摘 要】
：
The corrosion behavior of high-strength steel used for flexible riser exposed to CO2-saturated saline solution and CO2-saturated vapor environments was studied through immersion experiment and electrochemical corrosion experiment.The corrosion behavior an
【机 构】
：
State Key Laboratory of Rolling and Automation,Northeastern University, Shenyang 110819, China;Neptu
论文部分内容阅读
The corrosion behavior of high-strength steel used for flexible riser exposed to CO2-saturated saline solution and CO2-saturated vapor environments was studied through immersion experiment and electrochemical corrosion experiment.The corrosion behavior and mechanism of the tested steel were analyzed on the basis of corrosion kinetics,nature of corrosion products,corrosion product morphology,elemental distribution and polarization curves.The experimental results showed that the microstructure of the tested steel was bainitic microstructure.The corrosive activity of the tested steel exposed to CO2-saturated vapor environment was significantly lower than that exposed to CO2-saturated saline solution environment.On prolonging the exposure time,the corrosion rate gradually decreased,the corrosion heterogeneity increased,and the dimensions of FeCO3 crystals gradually became small.At later stages of corrosion,the corrosion current density decreased significantly and the anodic Tafel slope increased,indicating that the corrosion process was strongly inhibited.The corrosion mechanism of low-alloy steel with bainitic microstructure was proposed based on experimental results.
其他文献
The microstructural evolution of pure nickel treated by deep rolling (DR) technique with different indent depths was investigated by means of optical microscopy and transmission electron microscopy.The surface roughness,hardness and residual stress distri
The synergistic effect of NaC1 and SO2 on the atmospheric corrosion of zinc has been studied at equivalent total but different ratios of molar deposition rate under wet-dry cyclic conditions.The results show that the corrosion rates,corrosion morphologies
Carbon fiber reinforced plastics (CFRP) are promising lightweight materials for vehicle applications.316L is one of the most widely used types of austenite stainless steels and applied in lots of automotive applications.The existence of crevices will resu
The present work describes the effect of deposition potentials on structural,morphological,optical,electrical and photoconductivity responses of cuprous oxide (Cu2O) thin films deposited on fluorine-doped tin oxide glass substrate by employing electrodepo
The surface of AISI 1045 steel specimens was modified via two duplex surface treatments of (i) titanium diffusion coating followed by plasma nitriding (Ti-PN) and (ii) plasma nitriding followed by titanium diffusion coating (PN-Ti).A comparative study on
Type I hot corrosion behavior of SiO2-Al2O3-glass composite coating based on Ti-47Al-2Cr-2Nb substrate was investigated in the mixture salt of 25 wt％NaCl + 75 wt％Na2SO4 at 850 ℃.The results showed that there was a bidirectional ion exchange between compos
Mg-Zn-Zr series Mg alloys (ZK) are one of the most important commercial Mg alloys due to their good comprehensive mechanical properties.The phase equilibria of the Mg-Zn-Zr system at 400 ℃ covering the overall composition range were investigated by X-ray
In the present study,a quenching treatment prior to two-stage heat treatment was conducted on a Fe-0.28C-1.55Mn-2.06Al transformation-induced plasticity steel to tailor the final microstructure.Compared with the microstructure of the ferrite,bainite and b
The damage behaviors of a titanium matrix composite shaft under torsion loading were monitored using the acoustic emission technique.The composite shaft with SiC fibers at ± 45° orientations was prepared by the solid-state fabrication process.Both the tor
Ni-based self-lubricating composites containing a fixed amount of hexagonal boron nitride (h-BN) (5 wt％) and different amounts of graphene (0-1.5 wt％) were prepared by ultrasonic dispersion,high-energy ball milling,and spark plasma sintering.The effects o