本文通过慢拉伸应力腐蚀试验,对16MnR钢焊接接头在空气和H2S溶液中的应力腐蚀行为进行比较,从而研究H2S溶液对16MnR钢焊接接头的敏感性。
In this paper, the stress corrosion testing of 16MnR steel welded joints in air and H2S solution was compared by slow tensile stress corrosion test to study the sensitivity of H2S solution to 16MnR steel welded joints.