The compound metal oxide Lax Pby Mnz O used as support was prepared by the sol-gel method, and the catalyst in which Pd was used as active component and Sn as co-active component for direct synthesis of diphenyl carbonate (DPC) with heterogeneous catalytic reaction was obtained by co-calcination and precipitation respectively. The catalyst was characterized by XRD, SEM and TEM respectively. The specific surface area of catalysts was measured by ChemBET3000 instrument, and the activity of the catalysts was tested by the synthesis of DPC in a pressured reactor. The results showed that when the co-active component Sn was added by co-calcination method A, its loading content was equal to 14.43% and active component Pd was loaded by precipitation, the yield and selectivity of DPC could reach 26.78% and 99% respectively.
The compound metal oxide Lax Pby Mnz O used as support was prepared by the sol-gel method, and the catalyst in which Pd was used as an active component and Sn as co-active component for direct synthesis of diphenyl carbonate (DPC) with a heterogeneous catalytic The catalyst was characterized by XRD, SEM and TEM respectively. The specific surface area of catalysts was measured by ChemBET3000 instrument, and the activity of the catalysts was tested by the synthesis of DPC in a pressured reactor. The results showed that when the co-active component Sn was added by co-calcination method A, its loading content was equal to 14.43% and active component Pd was loaded by precipitation, the yield and selectivity of DPC could reach 26.78% and 99% respectively.