Highly efficient phosphors under vacuum ultraviolet excitation are still demanded for the development of plasma display panels and Hg-free fluorescent lamps. Th
【机 构】
:
School of Materials Science and Engineering,National Synchrotron Radiation Laboratory
论文部分内容阅读
Highly efficient phosphors under vacuum ultraviolet excitation are still demanded for the development of plasma display panels and Hg-free fluorescent lamps. The phosphors of Eu3+ doped (Y, Gd, Lu)BO3 were synthesized with solid state reaction method and the con-tents of Y3+, Gd3+, and Lu3+ for plasma display panel red phosphor were optimized under vacuum ultraviolet excitation. Two new potential candidates, which were (Y1-S-7TGdSLuT)BO3: Eu3+ (0
其他文献
Isometric heat capacity cv and isobaric heat capacity cp of Pt with stable and metastable phases were calculated by using pure element systematic theory. These
Effect of ion nitriding modification on surface hardness, corrosion resistance and magnetostriction of (Tb0.3Dy0.7)Fe1.95 alloy was investigated. Results demons
Unusual intense infrared-to-ultraviolet upconversion luminescence was observed in YF3:Yb3+(20%)/Tm3+(1%) nanocrystals under 980 nm excitation. The intense ultra
In the present work, the microstructures of A356 feedstock cast via a pipe consisting of partial inclined and partial vertical sections were investigated. The e
Pyrochlore oxides of general compositions, A2Zr2O7, where A is a 3+ cation (La to Lu), are promising candidate materials for ap-plications as high temperature t
The effects of mineral processing wastewater on sulfide minerals were investigated by flotation, infrared spectrometry and electrochemistry test. The results sh
The flow and concentration fields in a new style tubular stirred reactor were simulated by simulating the fluids dynamics(CFD), in which FLUENT software was use
It iS known that the strength of alloys can be successfully improved by rapid solidification. The paper presents a process where Cu-Cr-Sn-Zn lead frame alloy is
Steady-state corrosion and wear behaviors of two Al-bronzes, Cu-14Al-X and QAl9-4, in 5.0% H2SO4 solution were investigated. It is found that wear loss of bronz
Multilayer ceramic sheets composed of Li1.075Nb0.625Ti0.45O3 (LNT) layers and silver metal layers were fabricated by aqueous tape-casting method. LNT green tape