为改善Q235碳钢的耐蚀性,在其表面涂覆了1种环氧涂层。采用中性盐雾试验(NSS)、湿热试验、盐水全浸试验和电化学交流阻抗谱(EIS)对比了Q235钢涂覆前后的耐蚀性能。结果表明,Q
【机 构】
：
海聚高分子材料科技(广州)有限公司,天津盛杰科技发展有限公司,湖南科技大学机电工程学院,
论文部分内容阅读
为改善Q235碳钢的耐蚀性,在其表面涂覆了1种环氧涂层。采用中性盐雾试验(NSS)、湿热试验、盐水全浸试验和电化学交流阻抗谱(EIS)对比了Q235钢涂覆前后的耐蚀性能。结果表明,Q235钢涂覆后在盐水中的平均腐蚀速率仅有38.8 mg/(m2·h),下降了86.3%以上,低频阻抗数值增加了3个多数量级,耐蚀能力显著提高。
To improve the corrosion resistance of Q235 carbon steel, an epoxy coating is applied to its surface. The corrosion resistance of Q235 steel before and after coating was compared by neutral salt spray test (NSS), wet heat test, salt water immersion test and electrochemical impedance spectroscopy (EIS). The results showed that the average corrosion rate of Q235 steel in brine was only 38.8 mg / (m2 · h), decreased by 86.3% and the value of low frequency impedance increased by more than 3 orders of magnitude, and the corrosion resistance was significantly improved.
其他文献
通过示差扫描量热仪、力学性能测试及电镜分析等研究了端羧基丁腈橡胶(CTBN)和核壳橡胶(CSR)增韧改性环氧树脂(EP)体系的结构与增韧改性效果,结果表明:CTBN和CSR都能显著提高
采用DSC研究了以双氰胺/取代脲为潜伏型中温固化体系的三官能团环氧树脂TDE-85的固化反应动力学,探讨了反应机理并确定了最佳的固化工艺参数.结果表明,固化温度＜ 140℃时,受扩
本文总结了樱花的扦插、嫁接、分株繁殖、组织培养等无性繁殖技术。经过对各种文献的分析得出，樱花扦插须在一定浓度的生长素或生根粉剂处理下，保持较高的空气湿度，容易成活；樱花
语言教育类一等奖:陈要勤广州番禺职业技术学院日语学习者学习策略与口语能力关系的研究二等奖:盛文忠上海外国语大学类型学视阈下的汉日语语序对比研究——基于大规模语种库
本文介绍了建立500kV冲击高电压校准系统的目的、意义，基本组成及功能。着重对系统中所采用的测量方法，以及为保证系统可靠工作而采取的抗干扰措施进行了详细说明。最后分析了
In this paper, we introduce a message physical layer assisted message authentication (PAA) framework under public key infrastructure (PKI) in vehicular communic
本文简要叙述了时域反射测试系统的原理、结构及精密与通用两套系统的组建，并为此开展了电缆传输系统的相关测试研究，得到了一些初步结论。系统具有简单、快速和直观的突出优点
以苯酚、多聚甲醛为主要原料,氢氧化钠(NaOH)为催化剂合成了高固含量酚醛树脂,并以此制备了酚醛泡沫材料.通过粘度、氧指数、力学性能等测试研究了催化剂用量对酚醛树脂及酚
本文阐述了配热电偶或热电阻使用的、测温范围在(-60～ 1100)℃的数字温度显示仪表(包括数字显示和数字显示调节仪)的整机检定方法。
将皮秒分幅相机系统用于丝阵Z-pinch实验诊断中，获得了较好的实验结果，并对实验数据进行了初步的分析，利用皮秒分幅相机测得等离子体内爆速度达2 ×107cm/s，还测得了丝阵内爆的轴