In order to fabricate a kind of high strength particulate reinforced aluminum-matrix composites, the high strength aluminum alloy 7055 was selected as a matrix.
Using hydrous aluminum chloride (AlCl3·6H2O) and silicon ethoxide (Si (OC2H5)4) as raw materials, a kind of nano-sized mullite powder was synthesized with