The magnetic force images and surface topography images of sputtered Co/Au multilayer films in remnant state were measured by magnetic force microscopy. From the surface magnetic structures shown in the magnetic force images it can be seen that the domain patte and size vary with the increase of the thickness t of the non-ferromagnetic Au layer remarkably. With the measurements of the effective perpendicular anisotropy Ku and the domain period d, it was found that there are similar trends of d and Ku as functions of t. The variations of the domain patte and size were qualitatively interpreted in terms of magnetic domain theory, the theoretical relations of d and the domain wall energy ow vs t were calculated. As t = 8.5 AL(1AL=0.235nm), the largest ow is 11mJ/m2.