本文应用光学显微镜、电子显微镜、扫透电子显微镜和X-射线衍射仪对贝氏体型白口铸铁的组织结构和形态进行了观察和测试,同时还对上、下贝氏体在不同试验条件下的抗磨性和残余奥氏体在磨损过程中的行为进行了研究。
In this paper, the microstructure and morphology of bainitic white cast iron were observed and measured by optical microscope, electron microscope, scanning electron microscope and X-ray diffraction. At the same time, the microstructure and morphologies of bainite white cast iron were studied under different experimental conditions The wear resistance and the behavior of retained austenite in the wear process were studied.