【摘 要】
:
The surface nanostructures of commercial pure titanium was realized by the modified shot peening equipment commonly used in industry through the special treatme
【机 构】
:
School of Materials Science and Engineering,Beijing Aeronautical Manufacturing Technology Research I
论文部分内容阅读
The surface nanostructures of commercial pure titanium was realized by the modified shot peening equipment commonly used in industry through the special treatment process. The results show that high-energy-shot-peening(HESP) commonly used to prepare nanostructured surface layers can be achieved by the increase of pill size, pill speed, and treatment time in the commercial shot peening equipment. XRD, SEM and TEM were used to characterize the surface layer microstructure of treated specimens. The analytic results show that the main deformation mode of commercial pure Ti is twinning. At the beginning of deformation, the dislocations are formed and twins occur within or on plane, then twins in intersection plane appear, and at last the twin characteristics disappear in the surface layer after longer treatment time. The deformation layer depth increases with treatment time in a certain period when the pill size and speed are unchanged. And in the severe plastic deformation (SPD) layer in which the twins are not identified easily by using SEM, the nanocrystalline microstructures are found under TEM. The finest grain size in the surface layer is about 40 nm, and the depth of nanostructured layers is over 60 μm. The microhardness of the nanostructured surface layers is enhanced significantly after shot peening compared with that of the initial simple.
其他文献
A virtual instrument(Ⅵ) was developed to monitor the technological parameters in the process of brush plating, including coating thickness, brush-plating curre
The compound effect of Nd2Fe14B/Fe3B-Ferrite bonded magnets was studied.The result shows that the value ofβjHC obviously decreases with the ferrite content inc
The effect of enamel coating on long-term isothermal oxidation at 700 ℃ and cyclic oxidation at 800 ℃ in air and hot corrosion resistance of Ti-24Al-17Nb-0. 5
Joining techniques of dissimilar materials for lightweight multi-material automotive body structure were discussed. The joining of 1 .4 mm thickness steel and 2
The temporal variations in storm rainfall during the first rainy season (FRS) in South China (SC) are investigated in this study. The results show that the inte
By the decomposition of copper nitrate at 400 ℃, oriented islands of copperoxide crystals were successfully fabricated on the amorphous glass surface. X-ray di
High performance Sm2Fe17Nx magnetic powders were fabricated by ball-milling method and were compacted using spark plasma sintering(SPS) technique.Effects of pro
Organic coatings are widely used to control the corrosion of steel structure. The anticorrosive property of these coatings depends on their barrier properties,
Ba 3Zn Z Co 2 Z Fe 24 O 41 /SiO 2 ( Z varies from 0.0 to 1.2 in step of 0.4) microcrystalline glass ceramics were prepared by citrate
Electropulse modification (EPM) process, a new physical field method for improving the solidification structure of metals was introduced.Different from other re