对15NiCuMoNb5-6-4钢焊接接头进行不同回火参数的热处理,并对回火后焊接接头的力学性能进行了测试和分析。结果表明,提高回火温度和延长保温时间无法提高15NiCuMoNb5-6-4钢焊
【机 构】
：
陕西电力科学研究院材料技术研究所,西安北方华山机电有限公司计量理化中心,
论文部分内容阅读
对15NiCuMoNb5-6-4钢焊接接头进行不同回火参数的热处理,并对回火后焊接接头的力学性能进行了测试和分析。结果表明,提高回火温度和延长保温时间无法提高15NiCuMoNb5-6-4钢焊缝硬度,但焊缝硬度低于母材硬度时,焊接接头的拉伸强度和冲击性能指标依然可以满足设计要求。
The heat treatment of 15NiCuMoNb5-6-4 steel welded joint with different tempering parameters was carried out. The mechanical properties of the welded joint after tempering were tested and analyzed. The results show that the hardness of 15NiCuMoNb5-6-4 steel can not be improved by increasing the tempering temperature and prolonging the holding time. However, the tensile strength and impact performance of the welded joint can still meet the design requirements when the weld hardness is lower than that of the base metal.
其他文献
使用真空中频钎焊炉对1Cr18Ni9Ti进行焊接,钎料为HLCuNi30。采用钎料铺展面积测量法,得出该钎料钎焊该母材时的大体钎焊温度;采用钎焊接头楔形间隙图,对HLCuNi30钎料钎焊1Cr1
采用20%CO2+80%Ar气体保护MAG焊和焊条电弧焊对316L不锈钢进行焊接,通过对焊接接头进行拉伸、弯曲、硬度试验和显微组织观察,研究了焊接接头组织性能。结果表明,焊条电弧焊接
平衡液是医院常用的灭菌制剂,它由氯化钾、氯化钙、氯化镁和葡萄糖四种成分组成.文献[1]规定用家兔法检查其热原,而医院药检室由于受设备条件限制,用家兔法检查热源,困难很大
钎焊是硬质合金与钢基体结合的主要方法,而大批量生产时主要以高频感应钎焊为主。焊接过程中钎料润湿与填充不充分、焊接残余应力过大以及高脆性物质η相的生成是影响焊接接
请下载后查看，本文暂不支持在线获取查看简介。
Please download to view, this article does not support online access to view profile.
在用耐热温度数据记录仪测温实验的基础上,建立了网带式连续钎焊炉内钢坯升温过程的数学模型,利用有限元软件ANSYS对其温度场进行有限元数值模拟。通过计算出45钢坯料不同表
介绍了镁合金在汽车工业中的应用现状,分析了镁合金焊接的主要问题,综述了镁合金各种焊接方法的特点及研究现状,展望了镁合金焊接的发展趋势。
The application status of m
为了更好地规范畜禽屠宰加工，保证动物性食品安全，国家质检总局和国家标准化管理委员会于2006年9月29日颁布了国家标准GB/T 20551—2006《畜禽屠宰HACCP应用规范》，自2006年12月
在前期焊接试验参数优化基础上,通过自行研制的线性摩擦焊机焊接了两组TC4钛合金试件,其中对一组试件焊后进行630℃x3h的热处理,然后对焊态和热处理态焊接接头的组织和力学性
采用正交试验设计的方法,研究了电阻点焊热镀锌钢板时焊接时间t、焊接压力P及焊接电流I的优化匹配对焊点质量的影响权重。焊接接头拉伸和剥离试验分析表明,三种焊接工艺参数