Effect of La on emergence, growth and development of Isatis indigotica Fort and Festuca arundinacea seedlings was researched by pot experiments of inoculating Rhizoctonia solani and with the mixture of Rhizoctonia solani and Fusarium solani in disinfected soil after the seeds were soaked in the solution with different concentrations of La3+. The results indicated that infection rate decreased and there were significant disease controlling effects on seed rot, bud rot and root rot caused by pathogenic fungi when the seeds were soaked by La3+. Thus, the rates of emergence of Isatis indigotica Fort. And turfgrass Festuca arundinacea were increased. When La3+ concentration was in a proper range, the growth and development of plant seedlings were promoted. Spraying La on rice plants showed a significant controling effect on Rhizoctonia solani. Furthermore, the EC50 of La3+ performed 128.7 and 128.1 mg/L at 1 and 7 d after spraying La in rice plants, respectively. The EC50ofLa3+ performed in vivo (in rice plant) was lower than that in vitro (171.9 mg/L).
其他文献
A facile approach to preparing well-dispersed nanocrystals of BaCeO3 was developed by a combination of solvothermal and annealing processes. The precursor consi
A novel process for synthesis gas production over Circulating Fluidized Bed (CFB) using oxygen storage materials as oxygen carrier was reported. First, oxygen i
The Ni-CeO2 catalysts with different Ni contents were prepared by a co-precipitation method and used for Reverse Water Gas Shift (RWGS) reaction. 2wt.%Ni-CeO2 s
The modifying effect of La addition on primary phase Mg2Si in Mg-5Si alloys was investigated. The results showed that a proper amount of La could effectively mo
Different compositions of yttrium silicates coatings were deposited on SiC-C/C by plasma spraying and an outer borosilicate glass was applied on the yttrium sil
A synthesis of LaF3:0.04Yb3+,0.01Er3+ nanocrystals with oleic acid as a capping iigand was presented. The X-Ray Diffraction (XRD) pattern indicated that the pow
Degraded chitosan, with highly water-solubility, was obtained by the oxidation of chitosan with H2O2, and then reacted with furfural The final product coordinat
The luminescence of Eu2+ in BaMgSiO4 with BaB2O4 as flux was studied. The emission spectrum of the phosphor consisted of two bands, peaking at about 398 nm and
The nonuniform Yb-Er Codoped Al2O3 films were prepared oil SiO2/Si substrates using a medium frequency magnetron sputtering system. Two asymmetry targets in the
To improve the cyclic stability of La-Mg-Ni system alloy, as-cast La0.75Mg0.25Ni3.5Co0.2 alloy was annealed at 1123, 1223, and 1323 K for 10 h in 0.3 MPa argon.